PTS PCA-30G11-(V) 紫外线稳定、

PTS PCA-30G11-(V) PBT广泛地用于生产保险杠、化油器组件、挡泥板、扰流板、火花塞端子板、供油系统零件、仪表盘、汽车点火器、加速器及离合器踏板等部件。
PTS PCA-30G11-(V)   在相对湿度较高、十分潮湿的情况下,由于潮湿易引起塑性降低,电器节点处容易引起腐蚀,常可使用改性PBT。在80℃、90%相对湿度下,PBT仍能正常使用,并且效果很好。
原料颗粒图:3cb92a240a17ac78-f9799ed1752670e2-c32c41df3b96522cd99c152318c27c58  、
 
物性表:
 
Physical Properties Metric English Comments
Density  1.26 g/cc 0.0455 lb/in³ ASTM D792
Melt Flow  11 g/10 min
@Load 5.00 kg,
Temperature 250 °C
11 g/10 min
@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
 
Mechanical Properties Metric English Comments
Tensile Strength, Yield  62.0 MPa
@Thickness 3.17 mm
8990 psi
@Thickness 0.125 in
ASTM D638
Elongation at Break  6.0 %
@Thickness 3.17 mm
6.0 %
@Thickness 0.125 in
ASTM D638
Flexural Yield Strength  96.0 MPa
@Thickness 3.17 mm
13900 psi
@Thickness 0.125 in
ASTM D790
Flexural Modulus  2.86 GPa
@Thickness 3.17 mm
415 ksi
@Thickness 0.125 in
ASTM D790
Izod Impact, Notched  2.13 J/cm
@Thickness 3.17 mm
3.99 ft-lb/in
@Thickness 0.125 in
ASTM D256
 
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi)  99.0 °C 210 °F ASTM D648
UL RTI, Electrical  75.0 °C 167 °F  
UL RTI, Mechanical with Impact  75.0 °C 167 °F  
UL RTI, Mechanical without Impact  75.0 °C 167 °F  
Flammability, UL94    HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
 
  HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
 
 
Processing Properties Metric English Comments
Rear Barrel Temperature  257 - 279 °C 495 - 535 °F  
Middle Barrel Temperature  246 - 279 °C 475 - 535 °F  
Front Barrel Temperature  246 - 279 °C 475 - 535 °F  
Nozzle Temperature  246 - 279 °C 475 - 535 °F  
Melt Temperature  246 - 279 °C 475 - 535 °F  
Mold Temperature  71.1 - 93.3 °C 160 - 200 °F  
Drying Temperature  87.8 - 98.9 °C 190 - 210 °F 12 hours maximum
  98.9 °C 210 °F 4 hours minimum
Dew Point  -40.0 °C -40.0 °F Preferred
  <= -20.0 °C <= -4.00 °F  
Injection Pressure  110 - 138 MPa 16000 - 20000 psi  
Back Pressure  0.689 - 1.38 MPa 100 - 200 psi  
Shot Size  50 - 70 % 50 - 70 %  
Vent Depth  0.00203 - 0.00254 cm 0.000800 - 0.00100 in  
Screw Speed  40 - 70 rpm 40 - 70 rpm  
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-27632.html

免责声明: 本文 PTS PCA-30G11-(V) 紫外线稳定、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络