| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 26 g/10 min @Load 2.16 kg, Temperature 250 °C |
26 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM D638 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 5.40 kJ/m² | 2.57 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.380 mm |
HB @Thickness 0.0150 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||