TPV 8221-70 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | 2 mm, 15 sec; ISO 868 | ||
| Tensile Strength at Break | 6.80 MPa | 986 psi | Across Flow; ASTM D412 | ||
| Tensile Stress | 2.90 MPa @Strain 100 % |
421 psi @Strain 100 % |
Across Flow; ASTM D412 | ||
| Elongation at Break | 600 % | 600 % | Across Flow; ASTM D412 | ||
| Tear Strength | 25.1 kN/m | 143 pli | 73°C, Die C; ASTM D624 | ||
| Compression Set | 38 % | 38 % | 158°F, 22 hr; ASTM D395 | ||
| 58 % | 58 % | 257°F, 70 hr; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -62.2 °C | -80.0 °F | ASTM D746 | ||
| UL RTI, Electrical | 100 °C | 212 °F | UL 746 | ||
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746 | ||
| Flammability, UL94 | HB @Thickness 1.10 mm |
HB @Thickness 0.0433 in |
|||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 179 - 196 °C | 355 - 385 °F | |||
| Middle Barrel Temperature | 185 - 199 °C | 365 - 390 °F | |||
| Front Barrel Temperature | 191 - 204 °C | 375 - 400 °F | |||
| Nozzle Temperature | 191 - 210 °C | 375 - 410 °F | |||
| Die Temperature | 185 - 221 °C | 365 - 430 °F | Extrusion | ||
| Melt Temperature | 185 - 221 °C | 365 - 430 °F | Extrusion | ||
| 199 - 216 °C | 390 - 420 °F | Processing | |||
| Mold Temperature | 23.9 - 51.7 °C | 75.0 - 125 °F | Processing | ||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| De |
|||||
| Color | Natural Color | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 |
||||
1、 抗老化性耐候性耐热性能良好；
2、 抗永久变形性能
3、 抗张强度高、 高韧性和高回弹性；
4、 环保可重复使用；
TPV 8221-70 广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷、鞋类产品等. 上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询
TPV 8221-70 广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷、鞋类产品等. 上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询