原料颗粒图：
、
、物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 | ||
| Tensile Modulus | 2.75 GPa | 399 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|||
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 | ||
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | |||
| De |
|||||
| Back Pressure | Low | ||||
| Injection Speed | Medium - Fast | ||||