PBT 2401MT 是最坚韧的工程热塑材料之一,PBT 2401MT 它是半结晶材料,PBT 2401MT 有非常好的化学稳定性、机械强度、电绝缘特性
 PBT 2401MT  是最坚韧的工程热塑材料之一, PBT 2401MT  它是半结晶材料, PBT 2401MT  有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。PBT吸湿特性很弱。非增强型PBT的张力强度为50MPa,玻璃添加剂型的PBT张力强度为170MPa。玻璃添加剂过多将导致材料变脆。
原料颗粒图:391efecf63f2a35f-819bf9491e5a946e-7fab2fcef0edcbb890f589b443d15b82  、
 
物性表:
 
Physical Properties Metric English Comments
Density  1.31 g/cc 0.0473 lb/in³ ISO 1183
Linear Mold Shrinkage, Flow  0.018 - 0.020 cm/cm 0.018 - 0.020 in/in ISO 294-4
Melt Flow  20 g/10 min
@Load 2.16 kg,
Temperature 250 °C
20 g/10 min
@Load 4.76 lb,
Temperature 482 °F
(MVR) cm³/10min; ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress  30.0 MPa
@Strain 50.0 %
4350 psi
@Strain 50.0 %
50mm/min; ISO 527-2/1A
Tensile Strength, Yield  60.0 MPa 8700 psi 50mm/min; ISO 527-2/1A
Elongation at Break  >= 50 % >= 50 % 50mm/min; ISO 527-2/1A
Elongation at Yield  4.0 % 4.0 % 50mm/min; ISO 527-2/1A
Tensile Modulus  2.60 GPa 377 ksi 1mm/min; ISO 527-2/1A
Flexural Strength  80.0 MPa 11600 psi ISO 178
Flexural Modulus  2.50 GPa 363 ksi ISO 178
Izod Impact, Notched (ISO)  5.00 kJ/m² 2.38 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  NB NB ISO 179/1eU
   19.0 J/cm²
@Temperature -30.0 °C
90.4 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm² 2.86 ft-lb/in² ISO 179/1eA
   0.600 J/cm²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm IEC 60093
Surface Resistance  1.00e+15 ohm 1.00e+15 ohm IEC 60093
Dielectric Constant    3.5
@Frequency 1.00e+6 Hz
3.5
@Frequency 1.00e+6 Hz
IEC 60250
  4.0
@Frequency 100 Hz
4.0
@Frequency 100 Hz
IEC 60250
Dielectric Strength  23.0 kV/mm 584 kV/in IEC 60243-1
Dissipation Factor    0.0014
@Frequency 100 Hz
0.0014
@Frequency 100 Hz
IEC 60250
  0.022
@Frequency 1.00e+6 Hz
0.022
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear  110 µm/m-°C 61.1 µin/in-°F ISO 11359-2
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1,-2,-3
Transformation Temperature, Tg  60.0 °C 140 °F 10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi)  150 °C 302 °F ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)  55.0 °C 131 °F ISO 75-1, -2
Vicat Softening Point  190 °C 374 °F B50 (50°C/h 50N); ISO 306
Flammability, UL94  HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
UL94
Oxygen Index  20 % 20 % ISO 4589
 
Processing Properties Metric English Comments
Processing Temperature  20.0 - 50.0 °C 68.0 - 122 °F  
  65.0 - 93.0 °C 149 - 199 °F Cavity temperature
Feed Temperature  230 - 240 °C 446 - 464 °F  
Rear Barrel Temperature  230 - 240 °C 446 - 464 °F  
Middle Barrel Temperature  235 - 250 °C 455 - 482 °F  
Front Barrel Temperature  240 - 260 °C 464 - 500 °F  
Nozzle Temperature  250 - 260 °C 482 - 500 °F  
Zone 1  230 - 240 °C 446 - 464 °F  
Zone 2  235 - 250 °C 455 - 482 °F  
Zone 3  235 - 250 °C 455 - 482 °F  
Zone 4  240 - 260 °C 464 - 500 °F  
Die Temperature  250 - 260 °C 482 - 500 °F  
Melt Temperature  243 °C 469 °F Injection molding; ISO 294
  235 - 260 °C 455 - 500 °F  
Mold Temperature  65.6 - 93.3 °C 150 - 200 °F  
  82.0 °C 180 °F Injection molding; ISO 294
Injection Velocity  300 mm/sec 11.8 in/sec ISO 294
Drying Temperature  120 - 130 °C 248 - 266 °F  
Dry Time  4.00 hour 4.00 hour  
Moisture Content  0.020 % 0.020 % Necessary low maximum residual
Hold Pressure  48.0 MPa 6960 psi ISO 294
Back Pressure  0.000 - 0.345 MPa 0.000 - 50.0 psi  
Hot-Working Temperature  250 - 260 °C 482 - 500 °F  
 
Descriptive Properties
Injection molding Yes  
Injection speed medium-fast  
Longer pre-drying times/storage lower the temperature to 100° C until processed. <= 60 h
Processing conditions ISO 7792-2  
Processing Notes Fast Injection Speed  
  Medium Screw Speed
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-27966.html

免责声明: 本文 PBT 2401MT , 医学科技 、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4