TPE DGR 6050 NC/BK 物性表:
应用领域
上海松翰塑化科技有限公司供应产品,品质一流,TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话:13751253137 QQ:205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询
TPE DGR 6050 NC/BK 个别产品图片
TPE DGR 6050 NC/BK 物性表:
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 0.990 g/cc | 0.990 g/cc | ASTM D471; ISO 2781 | ||
Viscosity | 109000 cP @Shear Rate 300 1/s, Temperature 190 °C |
109000 cP @Shear Rate 300 1/s, Temperature 374 °F |
ASTM D3835 | ||
Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | |||
0.028 cm/cm | 0.028 in/in | ||||
Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |||
0.013 cm/cm | 0.013 in/in | ||||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 49 | 49 | Time of 5 seconds; ASTM D2240; ISO 48 | ||
Tensile Strength, Ultimate | 5.5080 MPa | 798.87 psi | After 7 days at 70°C; ASTM D412 ISO 37 | ||
5.8041 MPa | 841.82 psi | After 7 days at 100oC; ASTM D412 ISO 37 | |||
5.92 MPa | 859 psi | ASTM D412; ISO 37 | |||
Elongation at Break | 448 % | 448 % | ASTM D412; ISO 37 | ||
456.92 % | 456.92 % | After 7 days at 70°C; ASTM D412 ISO 37 | |||
470.4 % | 470.4 % | After 7 days at 100°C; ASTM D412 ISO 37 | |||
Modulus of Elasticity | 0.00199 GPa | 0.289 ksi | After 7 days at 70°C; ASTM D412 ISO 37 | ||
0.00214 GPa | 0.310 ksi | After 7 days at 100°C; ASTM D412 ISO 37 | |||
100% Modulus | 0.00205 GPa | 0.298 ksi | ASTM D412; ISO 37 | ||
Graves Tear Strength | 20.9 kN/m | 119 pli | (Die C) At 75°F (24°C); ASTM D624 | ||
Taber Abrasion, mg/1000 Cycles | 70 | 70 | Cs-17 Wheel, 1000 g Load; ASTM D3389 | ||
Compression Set | 19 % | 19 % | After 22 Hr at 75°F (24°C); ASTM D395; ISO 815 | ||
41 % @Temperature 70.0 °C |
41 % @Temperature 158 °F |
22 hrs.; ASTM D395; ISO 815 | |||
68 % @Temperature 100 °C |
68 % @Temperature 212 °F |
22 hrs.; ASTM D395; ISO 815 | |||
Tensile Set | 9.0 % | 9.0 % | 100% Tension; ASTM D412 | ||
Thermal Properties | Metric | English | Comments | ||
Brittleness Temperature | -67.8 °C | -90.0 °F | ASTM D746; ISO 812 | ||
Processing Properties | Metric | English | Comments | ||
Processing Temperature | 204 °C | 400 °F | |||
Rear Barrel Temperature | 188 - 199 °C | 370 - 390 °F | |||
Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |||
Front Barrel Temperature | 216 - 227 °C | 420 - 440 °F | |||
Nozzle Temperature | 204 - 221 °C | 400 - 430 °F | |||
Melt Temperature | 199 - 221 °C | 390 - 430 °F | |||
Mold Temperature | 43.3 - 54.4 °C | 110 - 130 °F | |||
Injection Pressure | 1.03 - 3.45 MPa | 150 - 500 psi | |||
Cycle Time - Injection | 0.50 - 2.0 sec | 0.50 - 2.0 sec | boost | ||
Screw Speed | 25 - 100 rpm | 25 - 100 rpm | |||
Cure Time | 0.167 - 0.333 min | 0.00278 - 0.00556 hour | Cooling Time | ||
De |
|||||
Fluid Resistance - Volume Change, % (ASTM D471) | -12 | After 7 Days in Water at 212°F (100°C) | |||
22 | After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C) | ||||
3 | After 7 Days in ASTM Oil No.1 at 212°F (100°C) | ||||
45 | After 7 Days in IRM 903 Oil No.3 at 212°F (100°C |
1.智能电子设备:智能手环、智能手腕带,手机保护套等等
2.洁具:花洒头、喷枪、排污管、软管等。
3.日常用品:手把类(刀具、梳子、剪刀、手提箱、牙刷柄等)、脚踏垫、冰格、餐桌垫、瓶盖内衬、背包底座及其他橡塑制品等。
4.体育器材:手把(高尔夫球、各种球拍、脚踏车、滑雪器材、滑冰器材等)、潜水器材(蛙鞋、蛙镜、呼吸管、手电筒等)、刹车块、运动护垫等。
5.工具材料:手把工具(螺丝起子,榔头、锤子等手柄)。
6.汽车配件:汽车挡泥板、排挡罩、汽车密封条、垫片、方向盘、防尘套、脚踏板、手柄、方向盘、防尘罩等。
7.文具用品:橡皮擦、笔套、垫片等。
8.医疗器材:吸球、仪器手把、轮子、束带、容器、垫圈、防毒面罩、医疗管,一次性输液器,洗耳球等及相关医疗用品。
9.电线电缆:电缆线外壳、连接器、插头被覆等。
10.脚轮包胶:手推车轮子、医用脚轮、工业脚轮等
11.资讯部件:游乐器方向盘、手把、鼠标被覆、衬垫、外壳被覆、光碟包装盒及其它软质防震零件等。
12.儿童玩具:直接注塑成型生产软胶玩具,超软玩具。
13.成人用品:超软成人充气娃娃,女性自慰棒,男性飞机杯等等兴趣用品。
14.园林工具:手板锯、高枝剪、鍬、铲修枝剪、整篱剪、园林锯、园林剪刀、草耙、钢叉、修枝剪、花具、雪铲、小锄、修枝锯、草剪等手柄包胶。