TPE 6150 BK 物性表：
应用领域
TPE 6150 BK 个别产品图片
TPE 6150 BK 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D471; ISO 2781 | ||
| Viscosity | 327000 cP @Shear Rate 300 1/s, Temperature 190 °C |
327000 cP @Shear Rate 300 1/s, Temperature 374 °F |
ASTM D3835 | ||
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | |||
| 0.021 cm/cm | 0.021 in/in | ||||
| Linear Mold Shrinkage, Transverse | 0.00 cm/cm | 0.00 in/in | |||
| 0.0040 cm/cm | 0.0040 in/in | ||||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 52 | 52 | Time of 5 seconds; ASTM D2240; ISO 48 | ||
| Tensile Strength, Ultimate | 5.86 MPa | 850 psi | ASTM D412; ISO 37 | ||
| 6.857 MPa | 994.5 psi | After 7 days at 70°C; ASTM D412 ISO 37 | |||
| 8.6150 MPa | 1249.5 psi | After 7 days at 100oC; ASTM D412 ISO 37 | |||
| Elongation at Break | 360 % | 360 % | ASTM D412; ISO 37 | ||
| 381.6 % | 381.6 % | After 7 days at 70°C; ASTM D412 ISO 37 | |||
| 417.6 % | 417.6 % | After 7 days at 100°C; ASTM D412 ISO 37 | |||
| Modulus of Elasticity | 0.00170 GPa | 0.247 ksi | After 7 days at 100°C; ASTM D412 ISO 37 | ||
| 0.00181 GPa | 0.263 ksi | After 7 days at 70°C; ASTM D412 ISO 37 | |||
| 100% Modulus | 0.00179 GPa | 0.260 ksi | ASTM D412; ISO 37 | ||
| Graves Tear Strength | 25.6 kN/m | 146 pli | (Die C) At 75°F (24°C); ASTM D624 | ||
| Taber Abrasion, mg/1000 Cycles | 144 | 144 | Cs-17 Wheel, 1000 g Load; ASTM D3389 | ||
| Compression Set | 19 % | 19 % | After 22 Hr at 75°F (24°C); ASTM D395; ISO 815 | ||
| 76 % @Temperature 70.0 °C |
76 % @Temperature 158 °F |
22 hrs.; ASTM D395; ISO 815 | |||
| 87 % @Temperature 100 °C |
87 % @Temperature 212 °F |
22 hrs.; ASTM D395; ISO 815 | |||
| Tensile Set | 3.4 % | 3.4 % | 100% Tension; ASTM D412 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -67.8 °C | -90.0 °F | ASTM D746; ISO 812 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 227 °C | 440 °F | |||
| Rear Barrel Temperature | 204 - 221 °C | 400 - 430 °F | |||
| Middle Barrel Temperature | 216 - 227 °C | 420 - 440 °F | |||
| Front Barrel Temperature | 227 - 238 °C | 440 - 460 °F | |||
| Nozzle Temperature | 227 - 249 °C | 440 - 480 °F | |||
| Melt Temperature | 227 - 254 °C | 440 - 490 °F | |||
| Mold Temperature | 43.3 - 54.4 °C | 110 - 130 °F | |||
| Injection Pressure | 1.03 - 3.45 MPa | 150 - 500 psi | |||
| Cycle Time - Injection | 0.50 - 2.0 sec | 0.50 - 2.0 sec | boost | ||
| Screw Speed | 25 - 100 rpm | 25 - 100 rpm | |||
| Cure Time | 0.167 - 0.333 min | 0.00278 - 0.00556 hour | Cooling Time | ||
| De |
|||||
| Fluid Resistance - Volume Change, % (ASTM D471) | 1 | After 7 Days in Water at 212°F (100°C) | |||
| 16 | After 7 Days in ASTM Oil No.1 at 212°F (100°C) | ||||
| 47 | After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C) | ||||
| 95 | After 7 Days in IRM 903 Oil No.3 at 212°F (100°C | ||||
1.智能电子设备：智能手环、智能手腕带，手机保护套等等
2.洁具：花洒头、喷枪、排污管、软管等。
3.日常用品：手把类(刀具、梳子、剪刀、手提箱、牙刷柄等)、脚踏垫、冰格、餐桌垫、瓶盖内衬、背包底座及其他橡塑制品等。
4.体育器材：手把(高尔夫球、各种球拍、脚踏车、滑雪器材、滑冰器材等)、潜水器材(蛙鞋、蛙镜、呼吸管、手电筒等)、刹车块、运动护垫等。
5.工具材料：手把工具(螺丝起子，榔头、锤子等手柄)。
6.汽车配件：汽车挡泥板、排挡罩、汽车密封条、垫片、方向盘、防尘套、脚踏板、手柄、方向盘、防尘罩等。
7.文具用品：橡皮擦、笔套、垫片等。
8.医疗器材：吸球、仪器手把、轮子、束带、容器、垫圈、防毒面罩、医疗管，一次性输液器，洗耳球等及相关医疗用品。
9.电线电缆：电缆线外壳、连接器、插头被覆等。
10.脚轮包胶：手推车轮子、医用脚轮、工业脚轮等
11.资讯部件：游乐器方向盘、手把、鼠标被覆、衬垫、外壳被覆、光碟包装盒及其它软质防震零件等。
12.儿童玩具：直接注塑成型生产软胶玩具，超软玩具。
13.成人用品：超软成人充气娃娃，女性自慰棒，男性飞机杯等等兴趣用品。
14.园林工具：手板锯、高枝剪、鍬、铲修枝剪、整篱剪、园林锯、园林剪刀、草耙、钢叉、修枝剪、花具、雪铲、小锄、修枝锯、草剪等手柄包胶。 上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询