TPU 5045D 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ASTM D412 |
| Tensile Stress | 9.03 MPa @Strain 100 % |
1310 psi @Strain 100 % |
ASTM D412 |
| 20.0 MPa @Strain 300 % |
2900 psi @Strain 300 % |
ASTM D412 | |
| Elongation at Break | 520 % | 520 % | ASTM D412 |
| Tear Strength | 100 kN/m | 571 pli | Die C; ASTM D412 |
| Taber Abrasion, mg/1000 Cycles | 28 | 28 | ASTM D1044 |
| Abrasion | 25 | 25 | mm3; DIN 53516 |
| Compression Set | 23 % @Temperature 22.8 °C, Time 79200 sec |
23 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D3995B |
| 43 % @Temperature 70.0 °C, Time 259000 sec |
43 % @Temperature 158 °F, Time 72.0 hour |
ASTM D3995B | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 147 °C | 297 °F | ASTM D1525 |
| Brittleness Temperature | -22.0 °C | -7.60 °F | ASTM D746 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 205 °C | 401 °F | Gate Temperature; Extrusion |
| 205 - 215 °C | 401 - 419 °F | Injection | |
| Rear Barrel Temperature | 190 °C | 374 °F | Injection |
| Middle Barrel Temperature | 200 °C | 392 °F | Injection |
| Front Barrel Temperature | 210 °C | 410 °F | Injection |
| Nozzle Temperature | 205 - 215 °C | 401 - 419 °F | Injection |
| Zone 1 | 190 °C | 374 °F | Extrusion |
| Zone 2 | 200 °C | 392 °F | Extrusion |
| Zone 3 | 210 °C | 410 °F | Extrusion |
| Die Temperature | 215 °C | 419 °F | Extrusion |
| Mold Temperature | 25.0 - 60.0 °C | 77.0 - 140 °F | Injection |
| Injection Velocity | >= 10.0 mm/sec | >= 0.394 in/sec | Injection |
| Drying Temperature | 85.0 °C | 185 °F | Injection |
| 85.0 °C | 185 °F | Extrusion | |
| Dry Time | 4.00 hour | 4.00 hour | Injection |
| 4.00 hour | 4.00 hour | Extrusion | |
| Back Pressure | 0.600 - 1.20 MPa | 87.0 - 174 psi | Injection |
| Clamp Pressure | 40.0 - 70.3 MPa | 5800 - 10200 psi | Injection |
| Screw Speed | 60 - 200 rpm | 60 - 200 rpm | Injection |
应用介绍
1．薄膜和片材（TPU具较好耐磨性、抗刺穿性、抗撕裂性、弹性、粘合性）（TPU薄膜应用在冬季服装、鞋类具有防寒、保暖、防水性能好等特性外还具有特别好的透气性）
2．管材（TPU具有高伸长率，良好耐水解和抗微生物性、耐油性、优异机械性能，如作消防水管内衬，输y油管气动软管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗纵向弯曲强度和低温冲击强度，其耐撕裂性和抗裂纹传播性是所有塑料中最好的。如作溜冰、滑雪靴、运动鞋、特种功能鞋等）
4．电线、电缆、光缆护套（TPU具良好耐磨性、耐环境、耐候性、耐腐蚀性、绝缘性、弹性和低温柔韧性等）
5．拉链片、高档塑料表带、表壳以及潜水表、礼品表等系列（TPU具有高弹、耐折、耐水性好手感舒适等）
6．机械制品和其它应用（如制造汽车部件、机械轴承、滚轮、输送带、橡塑筛网、工业胶管,垫圈,密封圈,游泳镜,冲浪板,表带,动物标牌,电器零部件,涂料,粘合剂,纤维等.)
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询