| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89 | 89 | ASTM D785 |
| Tensile Strength, Ultimate | 67.6 MPa | 9800 psi | ASTM D638 |
| Tensile Modulus | 2.96 GPa | 430 ksi | ASTM D638 |
| Flexural Strength | <= 98.6 MPa | <= 14300 psi | ASTM D790 |
| Flexural Modulus | 2.93 GPa | 425 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.187 W/m-K | 1.30 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.6 °C | 195 °F | annealed; ASTM D648 |
| Vicat Softening Point | 92.2 °C | 198 °F | 50°C/hr; 50N; ASTM D1525 |
| 101 °C | 213 °F | 50°C/hr; 10N; ASTM D1525 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 @Temperature 22.8 °C |
1.49 @Temperature 73.0 °F |
ND; ASTM D542 |
| Haze | <= 2.0 % @Thickness 3.17 mm |
<= 2.0 % @Thickness 0.125 in |
ASTM D1003 |
| Transmission, Visible | 92 % @Thickness 3.17 mm |
92 % @Thickness 0.125 in |
ASTM D1003 |
物理性能：聚甲基丙烯酸甲酯 （Polymethylmethacrylate，简称PMMA，英文Acrylic），又称做压克力或有机玻璃，在香港多称做阿加力胶，它的铸板聚合物的数均分子量一般为2.2×104，相对密度为1.19～1.20，折射率为1.482～1.521，吸湿度在0.5%以下，玻璃化温度为105℃。具有高透明度，低价格，易于机械加工等优点，是平常经常使用的玻璃替代材料。