| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50% R.H.; ISO 62 | ||
| Melt Flow | 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO2039 | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Tensile Stress | 10.0 MPa @Strain 0.200 %, Time 3.60e+7 sec |
1450 psi @Strain 0.200 %, Time 10000 hour |
ISO 899-1 | ||
| 12.0 MPa @Strain 0.200 %, Time 3.60e+6 sec |
1740 psi @Strain 0.200 %, Time 1000 hour |
ISO 899-1 | |||
| 15.0 MPa @Strain 0.200 %, Time 3600 sec |
2180 psi @Strain 0.200 %, Time 1.00 hour |
ISO 899-1 | |||
| 31.0 MPa @Strain 0.600 %, Time 3.60e+6 sec |
4500 psi @Strain 0.600 %, Time 1000 hour |
ISO 899-1 | |||
| 32.0 MPa @Strain 0.600 %, Time 3.60e+7 sec |
4640 psi @Strain 0.600 %, Time 10000 hour |
ISO 899-1 | |||
| 35.0 MPa @Strain 0.500 %, Time 3600 sec |
5080 psi @Strain 0.500 %, Time 1.00 hour |
ISO 899-1 | |||
| 55.0 MPa @Strain 1.80 %, Time 3.60e+7 sec |
7980 psi @Strain 1.80 %, Time 10000 hour |
ISO 899-1 | |||
| 55.0 MPa @Strain 1.40 %, Time 3.60e+6 sec |
7980 psi @Strain 1.40 %, Time 1000 hour |
ISO 899-1 | |||
| 58.0 MPa @Strain 0.800 %, Time 3600 sec |
8410 psi @Strain 0.800 %, Time 1.00 hour |
ISO 899-1 | |||
| Tensile Strength, Yield | 60.0 MPa @Temperature 120 °C |
8700 psi @Temperature 248 °F |
ISO 527 | ||
| 90.0 MPa @Temperature 80.0 °C |
13100 psi @Temperature 176 °F |
ISO 527 | |||
| 125 MPa @Temperature 40.0 °C |
18100 psi @Temperature 104 °F |
ISO 527 | |||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Modulus of Elasticity | 8.80 GPa | 1280 ksi | ISO 527 | ||
| 2.50 GPa @Temperature 140 °C |
363 ksi @Temperature 284 °F |
SIO 527 | |||
| 5.00 GPa @Temperature 100 °C |
725 ksi @Temperature 212 °F |
SIO 527 | |||
| 8.10 GPa @Temperature 40.0 °C |
1170 ksi @Temperature 104 °F |
SIO 527 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180 | ||
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180 | |||
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 | ||
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 | ||
| 0.880 J/cm² @Temperature -30.0 °C |
4.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |||
| Tensile Creep Modulus, 1000 hours | 5800 MPa | 841000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | ||
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| 600 V | 600 V | Test Solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C @Temperature 23.0 - 55.0 °C |
2.22 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 168 °C | 334 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ISO 75 | ||
| Vicat Softening Point | 160 °C | 320 °F | (50 °C/h / 50N) - B/50; ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
POM 的简介
聚甲醛是一种表面光滑，有光泽的硬而致密的材料，淡黄或白色，可在-40- 100°C温度范围内长期使用。它的耐磨性和自润滑性也比绝大多数工程塑料优越，又有良好的耐油，耐过氧化物性能。很不耐酸，不耐强碱和不耐紫外线的辐射。
POM 物理性质
聚甲醛的拉伸强度达70MPa，吸水性小，尺寸稳定，有光泽，这些性能都比尼龙好，聚甲醛为高度结晶的树脂，在热塑性树脂中是最坚韧的。具抗热强度，弯曲强度，耐疲劳性强度均高，耐磨性和电性能优良。
POM 聚甲醛的性能:
性 能 数 值
比重 1.43
熔点 175°C
伸强度（屈服） 70MPa
伸长率（屈服） 15%
（断裂） 15%
冲击强度（无缺口） 108KJ/m2
（带缺口） 7.6KJ/m2
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。