巴斯夫 POM N2320 003 UNC Q600_产品资讯

POM N2320 的物性表：

Physical Properties	Metric	English	Comments

Density	1.40 g/cc	0.0506 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C/50% R.H.; ISO 62
Melt Flow	8.8 g/10 min @Load 2.16 kg, Temperature 190 °C	8.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	145 MPa	21000 psi	358/30; ISO 2039-1
Tensile Strength	60.0 MPa @Time 864000 sec	8700 psi @Time 240 hour	Hot water storage of tensile bars at 130°C in an autoclave
	61.0 MPa @Time 450000 sec	8850 psi @Time 125 hour	Hot water storage of tensile bars at 130°C in an autoclave
	66.0 MPa @Time 0.000 sec	9570 psi @Time 0.000 hour	Hot water storage of tensile bars at 130°C in an autoclave
Tensile Stress	5.00 MPa @Strain 0.500 %, Time 3.60e+7 sec	725 psi @Strain 0.500 %, Time 10000 hour	ISO 899-1
	7.00 MPa @Strain 0.500 %, Time 360000 sec	1020 psi @Strain 0.500 %, Time 100 hour	ISO 899-1
	10.0 MPa @Strain 0.500 %, Time 3600 sec	1450 psi @Strain 0.500 %, Time 1.00 hour	ISO 899-1
	15.0 MPa @Strain 2.00 %, Time 3.60e+7 sec	2180 psi @Strain 2.00 %, Time 10000 hour	ISO 899-1
	17.0 MPa @Strain 1.50 %, Time 360000 sec	2470 psi @Strain 1.50 %, Time 100 hour	ISO 899-1
	19.0 MPa @Time 3600 sec, Strain 1.00 %	2760 psi @Time 1.00 hour, Strain 1.00 %	ISO 899-1
	25.0 MPa @Strain 4.00 %, Time 3.60e+7 sec	3630 psi @Strain 4.00 %, Time 10000 hour	ISO 899-1
	29.0 MPa @Strain 3.00 %, Time 360000 sec	4210 psi @Strain 3.00 %, Time 100 hour	ISO 899-1
	31.0 MPa @Time 3600 sec, Strain 2.00 %	4500 psi @Time 1.00 hour, Strain 2.00 %	ISO 899-1
Tensile Strength, Yield	65.0 MPa	9430 psi	50mm/min; ISO 527
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO 527
	35.0 MPa @Temperature 80.0 °C	5080 psi @Temperature 176 °F	ISO 527
	60.0 MPa @Temperature 40.0 °C	8700 psi @Temperature 104 °F	ISO 527
Elongation at Break	27 %	27 %	50mm/min; ISO 527
Elongation at Yield	9.4 %	9.4 %	50mm/min; ISO 527
Modulus of Elasticity	2.70 GPa	392 ksi	ISO 527
	1.00 GPa @Temperature 80.0 °C	145 ksi @Temperature 176 °F	ISO 899-1
	1.90 GPa @Temperature 60.0 °C	276 ksi @Temperature 140 °F	ISO 899-1
	3.00 GPa @Temperature 20.0 °C	435 ksi @Temperature 68.0 °F	ISO 899-1
Tensile Modulus	2.41 GPa @Thickness 1.50 mm, Temperature 30.0 °C	350 ksi @Thickness 0.0591 in, Temperature 86.0 °F
	2.59 GPa @Thickness 4.00 mm, Temperature 30.0 °C	376 ksi @Thickness 0.157 in, Temperature 86.0 °F
	2.60 GPa @Thickness 1.50 mm, Temperature 90.0 °C	377 ksi @Thickness 0.0591 in, Temperature 194 °F
	2.71 GPa @Thickness 4.00 mm, Temperature 90.0 °C	393 ksi @Thickness 0.157 in, Temperature 194 °F
	2.79 GPa @Thickness 1.50 mm, Temperature 120 °C	405 ksi @Thickness 0.0591 in, Temperature 248 °F
	2.81 GPa @Thickness 4.00 mm, Temperature 120 °C	408 ksi @Thickness 0.157 in, Temperature 248 °F
Izod Impact, Notched (ISO)	5.50 kJ/m²	2.62 ft-lb/in²	ISO 180/A
	6.00 kJ/m²	2.86 ft-lb/in²	ISO 180/A
Charpy Impact Unnotched	21.0 J/cm²	99.9 ft-lb/in²	ISO 179
	19.0 J/cm² @Temperature -30.0 °C	90.4 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 179
Tensile Creep Modulus, 1000 hours	1400 MPa	203000 psi	ISO 899

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+13 ohm	1.00e+13 ohm	IEC 60093
Dielectric Constant	3.8 @Frequency 100 Hz	3.8 @Frequency 100 Hz	IEC 60250
	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1
Dissipation Factor	0.0010 @Frequency 100 Hz	0.0010 @Frequency 100 Hz	IEC 60250
	0.0050 @Frequency 1.00e+6 Hz	0.0050 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test Solution A; IEC 60112
	600 V	600 V	Test Solution B; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	11.0 µm/m-°C @Temperature 23.0 - 55.0 °C	6.11 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	167 °C	333 °F
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75
Vicat Softening Point	150 °C	302 °F	(50 °C/h / 50N) - B/50; ISO 306

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 230 °C	374 - 446 °F	Injection-molding
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Descriptive Properties
Color	Natural
Commercial Status	Active America
FDA	21 CFR 177.2470
Impact Modified	No
NSF Std. 51	Yes
NSF Std. 61	Yes
Primary Processing Technique	Injection Molding

POM 的简介

POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。

POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。

POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。

POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。

POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。

POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。

POM 化学性质

POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度）。

POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。

POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。

POM 环境性能:

POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。

POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。　　

POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。

应用范围

POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。

POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。