| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ISO 2577 | ||
| Melt Flow | 6.622 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.622 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 164 MPa @Load 36.5 kg, Time 30.0 sec |
23800 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-2 | ||
| Modulus of Elasticity | 7.30 GPa | 1060 ksi | ISO 527-2 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 4500 MPa | 653000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | ||
| 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| 600 V | 600 V | Test solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 170 °C | 338 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ISO 75-2 | ||
| Vicat Softening Point | 160 °C | 320 °F | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | Hopper Throat | ||
| Zone 1 | 205 °C | 401 °F | Feed zone | ||
| Zone 2 | 205 °C | 401 °F | Compression | ||
| Zone 3 | 210 °C | 410 °F | Metering-zone | ||
| Zone 4 | 210 °C | 410 °F | Nozzle | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection-molding | ||
| 210 °C | 410 °F | Optimal | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 100 °C | 212 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| De |
|||||
| Commercial Status | Europe | ||||
| Peripheral Screw Speed | <0.3 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||
POM 的简介
POM强度、刚度高，弹性好，减磨耐磨性好。其力学性能优异，比强度可达50.5MPa，比刚度可达2650MPa，与金属十分接近。POM的力学性能随温度变化小，共聚POM比均聚POM的变化稍大一点。
POM的冲击强度较高，但常规冲击不及ABS和PC；POM对缺口敏感，有缺口可使冲击强度下降90%之多。
POM的疲劳强度十分突出，10交变载荷作用后，疲劳强度可达35MPa，而PA和PC仅为28MPa。
POM的蠕变性与PA相似，在20℃、21MPa、3000h时仅为2.3%，而且受温度的影响很小。
POM的摩擦因数小，耐磨性好（POM>PA66>PA6>ABS>HPVC>PS>PC），极限PV值很大，自润滑性好。
POM制品对磨时，高载荷作用时易产生类似尖叫的噪声。
POM 化学性质
POM 按分子链结构不同，聚甲醛可分为均聚甲醛和共聚甲醛，前者密度、结晶度、熔点都高，但是热稳定性差，加工温度窄（10度），对酸堿的稳定性略低；后者密度、结晶度、熔点较低，但热稳定性好，不易分解，加工温度宽（50度） 。
POM 不足之处在于：由受强酸腐蚀，耐侯差，粘合性差，热分解与软化温度接近，限氧指数小。它们广泛用于汽车工业，电子电器，机械设备等。还可以做水龙头、框窗、洗漱盆。
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。由于它还具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM 环境性能:
POM不耐强酸和氧化剂，对烯酸及弱酸有一定的稳定性。
POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。
应用范围
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。当温度超过一定限度或熔体受热时间过长，会引起分解。
POM具有较好的综合性能，在热塑性塑料中是最坚硬的，是塑料材料中力学性能最接近金属的品种之一，其抗张强度、弯曲强度、耐疲劳强度，耐磨性和电性都十分优良，可在-40度--100度之间长期使用。