SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
Categories: Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Unreinforced
Material Notes: Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
SABIC PC/ABS C6200Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc 1.18 g/cc ASTM D 792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
@Thickness 3.20 mm 0.0040 - 0.0060 in/in
@Thickness 0.126 in SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
@Thickness 3.20 mm 0.0040 - 0.0060 in/in
@Thickness 0.126 in SABIC Method
Melt Flow 14.5 g/10 min
@Load 2.16 kg,
Temperature 260 °C 14.5 g/10 min
@Load 4.76 lb,
Temperature 500 °F ASTM D 1238
Spiral Flow 68.58 cm
@Temperature 260 °C 27.00 in
@Temperature 500 °F 10 ips,3.175 X 1524 mm; -
SABIC PC/ABS C6200 Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.0 MPa 9570 psi Type I, 50 mm/min; ASTM D 638
Elongation at Break 50 % 50 % Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 103 MPa 14900 psi 2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 2.68 GPa 389 ksi 2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 5.34 J/cm
@Temperature 23.0 °C 10.0 ft-lb/in
@Temperature 73.4 °F ASTM D 256
Impact Test 54.0 J
@Temperature -30.0 °C 39.8 ft-lb
@Temperature -22.0 °F Instrumented Impact Energy @ peak; ASTM D 3763
61.0 J
@Temperature 23.0 °C 45.0 ft-lb
@Temperature 73.4 °F Instrumented Impact Energy @ peak; ASTM D 3763
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Surface Resistance >= 1.00e+15 ohm >= 1.00e+15 ohm ROA; IEC 60093
Dielectric Constant 2.7
@Frequency 1.00e+6 Hz 2.7
@Frequency 1.00e+6 Hz IEC 60250
2.8
@Frequency 50.0 - 60.0 Hz 2.8
@Frequency 50.0 - 60.0 Hz IEC 60250
Dielectric Strength 17.0 kV/mm
@Thickness 3.20 mm 432 kV/in
@Thickness 0.126 in in oil; IEC 60243-1
25.0 kV/mm
@Thickness 1.60 mm 635 kV/in
@Thickness 0.0630 in in oil; IEC 60243-1
35.0 kV/mm
@Thickness 0.800 mm 889 kV/in
@Thickness 0.0315 in in oil; IEC 60243-1
Dissipation Factor 0.0040
@Frequency 50.0 - 60.0 Hz 0.0040
@Frequency 50.0 - 60.0 Hz IEC 60250
0.0080
@Frequency 1.00e+6 Hz 0.0080
@Frequency 1.00e+6 Hz IEC 60250
Arc Resistance 60 - 120 sec 60 - 120 sec Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index 250 - 400 V 250 - 400 V PLC code 2; UL 746A
Hot Wire Ignition, HWI 30 - 60 sec 30 - 60 sec PLC code 2; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs >= 120 arcs surface, PLC code 0; UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min 3.15 - 5.91 in/min PLC code 3; UL 746A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
@Thickness 3.20 mm 189 °F
@Thickness 0.126 in unannealed; ASTM D 648
90.0 °C
@Thickness 6.40 mm 194 °F
@Thickness 0.252 in unannealed; ASTM D 648
UL RTI, Electrical 85.0 °C 185 °F UL 746B
UL RTI, Mechanical with Impact 85.0 °C 185 °F UL 746B
UL RTI, Mechanical without Impact 85.0 °C 185 °F UL 746B
Flammability, UL94 HB
@Thickness 0.710 mm HB
@Thickness 0.0280 in UL 94
V-1
@Thickness 1.21 mm V-1
@Thickness 0.0476 in UL 94
V-0
@Thickness 1.47 mm V-0
@Thickness 0.0579 in UL 94
5VB
@Thickness 2.00 mm 5VB
@Thickness 0.0787 in UL 94
5VA
@Thickness 3.40 mm 5VA
@Thickness 0.134 in UL 94
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS (Asia Pacific)
SABIC Innovative Plastics Cycoloy® C6600 PC+ABS
SABIC Innovative Plastics Cycoloy® C2800 PC+ABS
SABIC Innovative Plastics Cycoloy® C2950HF PC+ABS
SABIC Innovative Plastics Cycoloy® C2950 PC+ABS