| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 80x80x1mm, at 23°C and 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.65 % | 0.65 % | 80x80x1mm, 23°C; ISO 62 |
| Melt Flow | 15.84 g/10 min @Load 2.16 kg, Temperature 190 °C |
15.84 g/10 min @Load 4.76 lb, Temperature 374 °F |
Calculated from Volume flow Rate: 11 cm3/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Break | 15 % | 15 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Yield | 8.0 % | 8.0 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Tensile Modulus | 3.10 GPa | 450 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA |
| 0.500 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
2.38 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 |
| 4.2 @Frequency 1e+6 Hz |
4.2 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | 80x80x1 mm; IEC 60243, part 1 |
| Dissipation Factor | 0.0025 @Frequency 100 Hz |
0.0025 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 |
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal, 30x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 11359, part 1/2 |
| Melting Point | 170 °C | 338 °F | DSC, 10 K/min, Molding compound; ISO 3146, method C1b |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 80x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 75, part 1/2 |
| Vicat Softening Point | 156 °C | 313 °F | VST/B/50, 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 306 |