类别：聚合物；热塑性；亚克力（PMMA）；聚苯乙烯（PS）；苯乙烯/甲基丙烯酸甲酯共聚物（SMMA）
材料说明：pmma 84 L是一种新的丙烯酸聚合物的atohaas增加注塑应用的材料范围内产生的类型。pmma 84 L是苯乙烯-甲基丙烯酸甲酯共聚物的研究是为了满足一个高性能的产品能够在抗裂性方面需要的应用。
突出特点：
清晰与辉煌
耐刮伤
易加工
紫外稳定性
耐家用洗涤剂和洗碗机循环
良好的抗裂性
典型应用：
沙拉碗，杯子，餐具及其他家庭用品，处理部分需要耐洗碗机循环。
医疗器械。
浴房配件。
物性表：
示图：物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Water Absorption | 1.0 % | 1.0 % | |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | Humidity Absorption |
| Melt Flow | 4.6 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.6 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50 mm/min |
| Elongation at Break | 6.0 % | 6.0 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1 mm/min |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2700 MPa | 392000 psi | |
| Tensile Creep Modulus, 1000 hours | 1800 MPa | 261000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
Dielectric Constant  |
3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
|
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Dissipation Factor |
0.040 @Frequency 1e+6 Hz |
0.040 @Frequency 1e+6 Hz |
|
| 0.050 @Frequency 100 Hz |
0.050 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 98.0 °C | 208 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1396427082
联系邮箱；1396427082@qq.com
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1396427082
联系邮箱；1396427082@qq.com