pmma zk-6亚克力成型和挤出复合
类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；丙烯酸，一般用途
材料说明：聚丙烯酸酯塑料加化合物专门制定提供增强的抗冲击性，韧性和耐化学性，不失清晰。这些化合物结合最大的影响性能与清晰的标准有机玻璃材料的预期。聚丙烯酸酯塑料加化合物抵抗室外风化的不利影响，经过长时间的户外暴露也能保留其物理性能和较好的外观。
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
| Melt Flow | 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.7 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 40 | 40 | ASTM D785 |
| Tensile Strength, Yield | 43.4 MPa | 6290 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ASTM D638 |
| Flexural Strength | 59.3 MPa | 8600 psi | ASTM D790 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 6.35 mm, Temperature 0.000 °C |
0.700 ft-lb/in @Thickness 0.250 in, Temperature 32.0 °F |
ASTM D256 |
| 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 72.0 µm/m-°C @Temperature 0.000 - 100 °C |
40.0 µin/in-°F @Temperature 32.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 91.5 % | 91.5 % | ASTM D1003 |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com