| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-2/1A |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.20 kJ/m² | 2.00 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 60000 ohm-cm | 60000 ohm-cm | IEC 60093 |
| Surface Resistance | 1000 ohm | 1000 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | |
| Mold Temperature | 77.0 - 93.0 °C | 171 - 199 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 75.8 - 110 MPa | 11000 - 16000 psi | |