| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 80x80x1mm, at 23°C and 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | 80x80x1mm, 23°C; ISO 62 |
| Melt Flow | 5.32 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.32 g/10 min @Load 4.76 lb, Temperature 374 °F |
Calculated from Volume flow Rate: 4 cm3/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 105 MPa | 15200 psi | 30 sec value, 20x20x4 mm; ISO 2039, part 1; applied load 358 N |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Break | >= 40 % | >= 40 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 50 mm/min |
| Tensile Modulus | 2.10 GPa | 305 ksi | multi-purpose test specimen (ISO 3167); ISO 527, part 1/2; test speed 1 mm/min |
| Flexural Modulus | 2.00 GPa | 290 ksi | 80x10x4mm from multi-purpose test specimen (ISO 3167); ISO 178 |
| Charpy Impact Unnotched | 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU |
| NB @Thickness 4.00 mm, Temperature 23.0 °C |
NB @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA |
| 1.40 J/cm² @Thickness 4.00 mm, Temperature 23.0 °C |
6.66 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F |
80x10x4 m from multi-purpose test specimen (ISO 3167); ISO 179 1eA | |
| Penetration | 10 | 10 | mm, deformation damage, 60x60x3mm; ISO 6603, part 2 |
| 30 | 30 | J, work to damage, 60x60x3 mm; ISO 6603, part 2 | |
| Tensile Creep Modulus, 1 hour | 1800 MPa | 261000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi | multi-purpose test specimen (ISO 3167); ISO 899, part 1 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 |
| 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
80x80x1 mm; IEC 60250 |
| 0.0060 @Frequency 1e+6 Hz |
0.0060 @Frequency 1e+6 Hz |
80x80x1 mm; IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 131 °F |
Longitudinal, 30x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 11359, part 1/2 |
| Melting Point | 166 °C | 331 °F | DSC, 10 K/min, Molding compound; ISO 3146, method C1b |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 80x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 75, part 1/2 |
| Vicat Softening Point | 130 °C | 266 °F | VST/B/50, 10x10x4 mm from multi-purpose test specimen (ISO 3167); ISO 306 |