类别：聚合物；热塑性塑料；丙烯酸（有机玻璃）；乙烯基（聚氯乙烯）；聚氯乙烯/丙烯酸系合金
材质说明：高冲击防火板
用途：设备外壳，如影印机、仪表板、电脑、键盘、电话等。设备如自动售货机，风管隐蔽部位，烤架。矫形外科用支架，医疗器械零件，在储存显示器，电气设备
特点：优质的成形性很深或很难形成零件或良好的完成细节是必需的。KYDEX 100比大多数其他热塑性塑料导致部件变形时少装更多的刚性。提供抗破损。符合热塑性材料的耐化学性的最高标准。通过美国保险商实验室公司标准94 V-0和5V和UL 746C所有仪表和颜色识别。通过机动车辆安全标准（MVSS 302）。辐射板：22.5按照ASTM E162
制作：优异的成形性能，导致均匀壁厚和清晰的细节，再加上易于加工和制造使用传统的方法，进一步扩大成品零件的可能性。
物性表：
图：物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hrs.; ASTM D570 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | 7 days; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 94 | 94 | ASTM D785 |
| Hardness, Shore D | 77 | 77 | ASTM D2240 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 39.6 MPa | 5750 psi | ASTM D638 |
| Elongation at Break | 160 % | 160 % | |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 2.39 GPa | 347 ksi | ASTM D790 |
| Compressive Yield Strength | 55.2 MPa | 8000 psi | ASTM D695 |
| Ultimate Bearing Strength | 37.9 MPa | 5500 psi | ASTM D593 |
| Shear Strength | 31.0 MPa | 4500 psi | ASTM D732 |
Izod Impact, Notched  |
1.07 J/cm @Temperature 0.000 °C |
2.00 ft-lb/in @Temperature 32.0 °F |
ASTM D256 |
| 9.53 J/cm @Temperature 23.0 °C |
17.9 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Tensile Impact Strength | 158 kJ/m² | 75.0 ft-lb/in² | ASTM D1822 |
| Taber Abrasion, mg/1000 Cycles | 0.038 | 0.038 | ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant |
2.46 @Frequency 8.00e+8 Hz |
2.46 @Frequency 8.00e+8 Hz |
ASTM D150 |
| 2.8 @Frequency 1e+9 Hz |
2.8 @Frequency 1e+9 Hz |
ASTM D150 | |
| 3.4 @Frequency 60 Hz |
3.4 @Frequency 60 Hz |
ASTM D150 | |
| Dielectric Strength | >= 16.9 kV/mm | >= 430 kV/in | ASTM D149 |
| Dissipation Factor |
0.013 @Frequency 1e+9 Hz |
0.013 @Frequency 1e+9 Hz |
ASTM D150 |
| 0.022 @Frequency 60 Hz |
0.022 @Frequency 60 Hz |
ASTM D150 | |
| 0.023 @Frequency 8.00e+8 Hz |
0.023 @Frequency 8.00e+8 Hz |
ASTM D150 | |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V @Thickness 3.05 mm |
>= 600 V @Thickness 0.120 in |
UL PLC 0 |
| Hot Wire Ignition, HWI | 60 - 120 sec @Thickness 2.03 - 6.33 mm |
60 - 120 sec @Thickness 0.0799 - 0.249 in |
UL PLC 1 |
| High Amp Arc Ignition, HAI | 30 - 60 arcs @Thickness 1.57 - 6.33 mm |
30 - 60 arcs @Thickness 0.0618 - 0.249 in |
UL PLC 2 |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min @Thickness 1.57 - 6.33 mm |
>= 5.91 in/min @Thickness 0.0618 - 0.249 in |
UL PLC 4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.6 µm/m-°C @Temperature 16.0 °C |
42.0 µin/in-°F @Temperature 60.8 °F |
R&H P-4 |
| Specific Heat Capacity | 1.21 J/g-°C | 0.289 BTU/lb-°F | R&H P-37 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | annealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C @Thickness 1.57 - 6.33 mm |
122 °F @Thickness 0.0618 - 0.249 in |
|
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 1.57 - 6.33 mm |
122 °F @Thickness 0.0618 - 0.249 in |
|
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 1.57 - 6.33 mm |
122 °F @Thickness 0.0618 - 0.249 in |
|
| Flammability, UL94 | V-0 | V-0 | V-0, 5V; Underwriter's Lab; UL Standard 94 |
| Oxygen Index | 37.5 % | 37.5 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 163 - 200 °C | 325 - 392 °F | Forming Temperature |