| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Kasei Method |
| Melt Flow | 22 g/10 min | 22 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 45 % | 45 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB | |