类别：聚合物；热塑性弹性体，热塑性弹性体；苯乙烯类热塑性弹性体；
材料说明：2系列推荐用于极性热塑性塑料具有优异的附着力的应用等三，ASA，PMMA。该化合物可在自然和黑色的颜色。
典型应用：保险杠，门槛，功能与设计要素，索环，手柄（手动工具和电动工具等），密封件，拇指轮
物质优势：，易着色（天然颜色的化合物），优异的附着力，优良的加工行为，插入成型可能，软触摸，适合汽车内饰，抗紫外。
加工方法：挤出成型，注塑成型
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN EN ISO 1183-1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 48 | 48 | DIN ISO 7619 | ||
| Tensile Strength | 3.50 MPa | 508 psi | DIN 53504/ISO 37 | ||
| Elongation at Break | 350 % | 350 % | DIN 53504/ISO 37 | ||
| Tear Strength | 10.0 kN/m | 57.1 pli | DIN ISO 34-1 | ||
| Peel Strength | 2.50 kN/m | 14.3 pli | PMMA; D41 1916 | ||
| 3.00 kN/m | 17.1 pli | ASA; D41 1916 | |||
| 3.50 kN/m | 20.0 pli | SAN; D41 1916 | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 160 °C | 320 °F | Injection | ||
| 200 °C | 392 °F | Extrusion | |||
| Middle Barrel Temperature | 180 °C | 356 °F | Extrusion | ||
| 180 °C | 356 °F | Injection | |||
| Front Barrel Temperature | 160 °C | 320 °F | Extrusion | ||
| 200 °C | 392 °F | Injection | |||
| Die Temperature | 190 - 210 °C | 374 - 410 °F | Extrusion | ||
| Head Temperature | 180 °C | 356 °F | Extrusion | ||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection, A temperature exceeding 80 °C (175 °F) should be avoided | ||
Drying Temperature  |
60.0 - 80.0 °C @Time 7200 - 14400 sec |
140 - 176 °F @Time 2.00 - 4.00 hour |
Injection | ||
| 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
Extrusion | |||
| Injection Pressure | 20.0 - 100 MPa | 2900 - 14500 psi | Injection | ||
| Back Pressure | 1.97 - 4.90 MPa | 285 - 710 psi | Injection | ||
| De |
|||||
| Color | Black | ||||
| Hotrunner | 180-220°C | The runner should be empty after a maximum of 2 - 3 shots. | |||
| Max Cylinder Temperature | 220°C | Injection | |||
| 230°C | Extrusion |
||||