| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | 24 hours at 73°C; ASTM D570 |
| Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | ASTM D955 |
| Melt Flow | 27 g/10 min @Load 2.16 kg, Temperature 190 °C |
27 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 82 | 82 | ASTM D785 |
| Tensile Strength, Yield | 61.8 MPa | 8960 psi | 23°C; 50% RH; ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Flexural Yield Strength | 91.2 MPa | 13200 psi | 23°C; 50% RH; ASTM D570 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 23°C; 50%RH; ASTM D570 |
| Izod Impact, Notched | 0.588 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 240 sec | 240 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.7937 mm |
HB @Thickness 0.03125 in |
UL94 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | |
| Front Barrel Temperature | 190 - 215 °C | 374 - 419 °F | |
| Nozzle Temperature | 190 - 215 °C | 374 - 419 °F | |
| Melt Temperature | 200 - 225 °C | 392 - 437 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Dry Time | 3 - 6 hour | 3 - 6 hour | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | |
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM N127 图：