| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ISO 2577 | ||
| Melt Flow | 6.622 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.622 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 164 MPa @Load 36.5 kg, Time 30.0 sec |
23800 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-2 | ||
| Modulus of Elasticity | 7.30 GPa | 1060 ksi | ISO 527-2 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 4500 MPa | 653000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | ||
| 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0040 @Frequency 100 Hz |
0.0040 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| 600 V | 600 V | Test solution B; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 | ||
| Melting Point | 170 °C | 338 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 110 °C | 230 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 161 °C | 322 °F | ISO 75-2 | ||
| Vicat Softening Point | 160 °C | 320 °F | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | Hopper Throat | ||
| Zone 1 | 205 °C | 401 °F | Feed zone | ||
| Zone 2 | 205 °C | 401 °F | Compression | ||
| Zone 3 | 210 °C | 410 °F | Metering-zone | ||
| Zone 4 | 210 °C | 410 °F | Nozzle | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection-molding | ||
| 210 °C | 410 °F | Optimal | |||
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 100 °C | 212 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| De |
|||||
| Commercial Status | Europe | ||||
| Peripheral Screw Speed | <0.3 m/s | ||||
| Primary Processing Technique | Injection Molding | ||||