| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | With Flow; ISO 2577 |
| 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 190 °C |
14 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | <= 60.0 MPa | <= 8700 psi | ISO/R527 |
| Elongation at Yield | 10 % | 10 % | ISO/R527 |
| Flexural Strength | <= 80.0 MPa | <= 11600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 150 °C @Load 5.001 kg |
302 °F @Load 11.03 lb |
50°C/h; ISO 306 |