| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 27 % | 27 % | Type I, 5 mm/min; ASTM D638 |
| 32 % | 32 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 12 % | 12 % | Type I, 5 mm/min; ASTM D638 |
| 13 % | 13 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.52 GPa | 365 ksi | 1 mm/min; ISO 527 |
| 2.58 GPa | 374 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| Flexural Modulus | 2.21 GPa | 321 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.21 GPa | 321 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.410 J/cm | 0.768 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.71 J/cm | 16.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.27 | 0.27 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.13 | 0.13 | ASTM D3702 Modified |
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 132 µm/m-°C @Temperature -30.0 - 30.0 °C |
73.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 124 µm/m-°C @Temperature -30.0 - 30.0 °C |
68.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 151 °C @Thickness 3.20 mm |
304 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM KL003LH 图：