| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.025 cm/cm | 0.025 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 7.4 % | 7.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 18.1 x 10-8 mm³/N-M | 9.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 114 µm/m-°C @Temperature 23.0 - 60.0 °C |
63.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 116 µm/m-°C @Temperature 23.0 - 60.0 °C |
64.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
POM KA000M 图：