类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋，品位的影响
材料说明：具有非常低的排放钢化中高粘度缩醛均聚物
聚甲醛300te NC010是中高粘度增韧缩醛均聚物具有非常低的挥发性有机化合物的排放。加工方法包括注塑成型。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4 2577 | ||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527-1/-2 | ||
| Elongation at Break | 37 % | 37 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 20 % | 20 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ISO 75-1/-2 | ||
| Flame Spread | 46 mm/min @Thickness 1.00 mm |
1.8 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Additives | Lubricants | ||||
| Release agent | |||||
| Delivery form | Pellets | ||||
| Emissions | <2 mg/kg | VDA 275 | |||
| Part Marking Code | >POM-I< | ISO 11469 | |||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | POM-I | ISO 1043 |
|||