杜邦高性能聚合物聚甲醛POM 510GR nc000_产品资讯

杜邦高性能聚合物聚甲醛（POM）510GR nc000 缩醛

类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，玻璃纤维增强

材料说明：10%玻璃纤维介质粘度缩醛均聚物

聚甲醛聚甲醛03510GR是10%玻璃纤维增强聚甲醛均聚物注射成型。具有高强度的刚度和较高的变形温度和良好的抗蠕变性能。

物性表：

Physical Properties	Metric	English	Comments

Density	1.49 g/cc	0.0538 lb/in³	ISO 1183
Water Absorption	1.1 % @Thickness 2.00 mm	1.1 % @Thickness 0.0787 in	Sim. to ISO 62
Moisture Absorption	0.160 % @Thickness 2.00 mm	0.160 % @Thickness 0.0787 in	Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.014 cm/cm	0.014 in/in	ISO 294-4 2577
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	95.0 MPa	13800 psi	ISO 527-1/-2
Tensile Stress	7.325 MPa @Strain 0.100 %, Temperature 23.0 °C	1062 psi @Strain 0.100 %, Temperature 73.4 °F	ISO 11403-1 -2
	38.14 MPa @Strain 0.700 %, Temperature 23.0 °C	5531 psi @Strain 0.700 %, Temperature 73.4 °F	ISO 11403-1 -2
	58.68 MPa @Strain 1.20 %, Temperature 23.0 °C	8511 psi @Strain 1.20 %, Temperature 73.4 °F	ISO 11403-1 -2
	74.43 MPa @Strain 1.70 %, Temperature 23.0 °C	10800 psi @Strain 1.70 %, Temperature 73.4 °F	ISO 11403-1 -2
	108.0 MPa @Strain 3.40 %, Temperature 23.0 °C	15660 psi @Strain 3.40 %, Temperature 73.4 °F	ISO 11403-1 -2
Elongation at Break	4.3 %	4.3 %	ISO 527-1/-2
Tensile Modulus	5.50 GPa	798 ksi	ISO 527-1/-2
Flexural Modulus	4.80 GPa	696 ksi	ISO 178
Secant Modulus	3.56 GPa @Strain 2.80 %, Temperature 23.0 °C	516 ksi @Strain 2.80 %, Temperature 73.4 °F	ISO 11403-1 -2
	4.04 GPa @Strain 2.10 %, Temperature 23.0 °C	586 ksi @Strain 2.10 %, Temperature 73.4 °F	ISO 11403-1 -2
	4.67 GPa @Strain 1.40 %, Temperature 23.0 °C	678 ksi @Strain 1.40 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.45 GPa @Strain 0.700 %, Temperature 23.0 °C	790 ksi @Strain 0.700 %, Temperature 73.4 °F	ISO 11403-1 -2
	7.325 GPa @Strain 0.100 %, Temperature 23.0 °C	1062 ksi @Strain 0.100 %, Temperature 73.4 °F	ISO 11403-1 -2
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²	ISO 179/1eU
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179/1eA
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	4800 MPa @Time 3600 sec	696000 psi @Time 1.00 hour	ISO 899-1
Tensile Creep Modulus, 1000 hours	3500 MPa @Time 3.60e+6 sec	508000 psi @Time 1000 hour	ISO 899-1

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	IEC 60250
	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C	38.9 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	174 °C	345 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	164 °C	327 °F	ISO 75-1/-2
Vicat Softening Point	160 °C	320 °F	50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10

Descriptive Properties
Additives	Release agent
Delivery form	Pellets
Part Marking Code	>POM-GF10<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-GF-10	ISO 1043
UL recognition	UL

图：