  4. 杜邦高性能聚合物聚甲醛POM fg100p NC010

杜邦高性能聚合物聚甲醛POM fg100p NC010

POM fg100p NC010 材料说明：用于食品接触应用程序开发的高粘度缩醛均聚物 聚甲醛fg100p是用容易填补模具改进热稳定性高粘度缩醛均聚物。
 杜邦高性能聚合物聚甲醛（POM）®fg100p NC010乙缩醛
类别：聚合物；热塑性；聚甲醛（POM）；缩醛均聚物，无筋
材料说明：用于食品接触应用程序开发的高粘度缩醛均聚物
聚甲醛fg100p是用容易填补模具改进热稳定性高粘度缩醛均聚物。
物性表：

 
Physical Properties Metric English Comments
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183
Water Absorption  1.4 %
@Thickness 2.00 mm		 1.4 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.300 %
@Thickness 2.00 mm		 0.300 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   138000 cP
@Shear Rate 5000 1/s,
Temperature 230 °C		 138000 cP
@Shear Rate 5000 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  153500 cP
@Shear Rate 5000 1/s,
Temperature 215 °C		 153500 cP
@Shear Rate 5000 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  170500 cP
@Shear Rate 5000 1/s,
Temperature 200 °C		 170500 cP
@Shear Rate 5000 1/s,
Temperature 392 °F		 ISO 11403-1 -2
  702600 cP
@Shear Rate 500 1/s,
Temperature 230 °C		 702600 cP
@Shear Rate 500 1/s,
Temperature 446 °F		 ISO 11403-1 -2
  762300 cP
@Shear Rate 500 1/s,
Temperature 215 °C		 762300 cP
@Shear Rate 500 1/s,
Temperature 419 °F		 ISO 11403-1 -2
  814100 cP
@Shear Rate 500 1/s,
Temperature 200 °C		 814100 cP
@Shear Rate 500 1/s,
Temperature 392 °F		 ISO 11403-1 -2
Linear Mold Shrinkage, Flow  0.022 cm/cm 0.022 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.020 cm/cm 0.020 in/in ISO 294-4 2577
Melt Flow   1.9 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 1.9 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 cm³/10min; ISO 1133
  2.5 g/10 min
@Load 2.16 kg,
Temperature 190 °C		 2.5 g/10 min
@Load 4.76 lb,
Temperature 374 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  92 92 ISO 2039-2
Hardness, Rockwell R  120 120 ISO 2039-2
Tensile Stress   10.8 MPa
@Strain 1.10 %,
Temperature 90.0 °C		 1570 psi
@Strain 1.10 %,
Temperature 194 °F		 ISO 11403-1 -2
  27.2 MPa
@Strain 4.40 %,
Temperature 90.0 °C		 3950 psi
@Strain 4.40 %,
Temperature 194 °F		 ISO 11403-1 -2
  32.4 MPa
@Strain 7.60 %,
Temperature 90.0 °C		 4700 psi
@Strain 7.60 %,
Temperature 194 °F		 ISO 11403-1 -2
  33.6 MPa
@Strain 10.9 %,
Temperature 90.0 °C		 4870 psi
@Strain 10.9 %,
Temperature 194 °F		 ISO 11403-1 -2
  35.5 MPa
@Strain 2.00 %,
Temperature 40.0 °C		 5150 psi
@Strain 2.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  42.0 MPa
@Strain 2.40 %,
Temperature 23.0 °C		 6090 psi
@Strain 2.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  52.0 MPa
@Strain 2.40 %,
Temperature 0.000 °C		 7540 psi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  57.0 MPa
@Strain 8.00 %,
Temperature 40.0 °C		 8270 psi
@Strain 8.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  57.7 MPa
@Strain 2.30 %,
Temperature -20.0 °C		 8370 psi
@Strain 2.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  59.5 MPa
@Strain 14.0 %,
Temperature 40.0 °C		 8630 psi
@Strain 14.0 %,
Temperature 104 °F		 ISO 11403-1 -2
  62.1 MPa
@Strain 2.10 %,
Temperature -40.0 °C		 9010 psi
@Strain 2.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  63.6 MPa
@Strain 9.80 %,
Temperature 23.0 °C		 9220 psi
@Strain 9.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  65.5 MPa
@Strain 17.1 %,
Temperature 23.0 °C		 9500 psi
@Strain 17.1 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  73.73 MPa
@Strain 9.60 %,
Temperature 0.000 °C		 10690 psi
@Strain 9.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  76.54 MPa
@Strain 21.59 %,
Temperature 0.000 °C		 11100 psi
@Strain 21.59 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  80.2 MPa
@Strain 9.20 %,
Temperature -20.0 °C		 11600 psi
@Strain 9.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  82.8 MPa
@Strain 16.1 %,
Temperature -20.0 °C		 12000 psi
@Strain 16.1 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  92.8 MPa
@Strain 13.0 %,
Temperature -40.0 °C		 13500 psi
@Strain 13.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  95.5 MPa
@Strain 22.7 %,
Temperature -40.0 °C		 13900 psi
@Strain 22.7 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  70.0 MPa 10200 psi ISO 527-1/-2
Elongation at Break  45 % 45 % Nominal; ISO 527-1/-2
Elongation at Yield  25 % 25 % ISO 527-1/-2
Tensile Modulus  2.90 GPa 421 ksi ISO 527-1/-2
Flexural Strength  74.0 MPa
@Strain 3.50 %		 10700 psi
@Strain 3.50 %		 ISO 178
Flexural Modulus  2.60 GPa 377 ksi ISO 178
Shear Modulus   0.297 GPa
@Temperature 120 °C		 43.1 ksi
@Temperature 248 °F		 Dynamic; ISO 11403-1 -2
  0.6221 GPa
@Temperature 60.0 °C		 90.23 ksi
@Temperature 140 °F		 Dynamic; ISO 11403-1 -2
  0.8835 GPa
@Temperature 10.0 °C		 128.1 ksi
@Temperature 50.0 °F		 Dynamic; ISO 11403-1 -2
  1.0443 GPa
@Temperature -30.0 °C		 151.47 ksi
@Temperature -22.0 °F		 Dynamic; ISO 11403-1 -2
  1.4976 GPa
@Temperature -60.0 °C		 217.21 ksi
@Temperature -76.0 °F		 Dynamic; ISO 11403-1 -2
Secant Modulus 0.337 GPa
@Strain 19.5 %,
Temperature 23.0 °C		 48.9 ksi
@Strain 19.5 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.357 GPa
@Strain 7.00 %,
Temperature 100 °C		 51.8 ksi
@Strain 7.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.369 GPa
@Strain 9.90 %,
Temperature 80.0 °C		 53.5 ksi
@Strain 9.90 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.371 GPa
@Strain 25.9 %,
Temperature -40.0 °C		 53.9 ksi
@Strain 25.9 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.37375 GPa
@Strain 16.0 %,
Temperature 40.0 °C		 54.209 ksi
@Strain 16.0 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.453 GPa
@Strain 18.4 %,
Temperature -20.0 °C		 65.7 ksi
@Strain 18.4 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.512 GPa
@Strain 4.20 %,
Temperature 100 °C		 74.2 ksi
@Strain 4.20 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.624 GPa
@Strain 5.00 %,
Temperature 80.0 °C		 90.5 ksi
@Strain 5.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.64898 GPa
@Strain 9.80 %,
Temperature 23.0 °C		 94.128 ksi
@Strain 9.80 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  0.681 GPa
@Strain 2.10 %,
Temperature 100 °C		 98.8 ksi
@Strain 2.10 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.7125 GPa
@Strain 8.00 %,
Temperature 40.0 °C		 103.3 ksi
@Strain 8.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  0.714 GPa
@Strain 13.0 %,
Temperature -40.0 °C		 104 ksi
@Strain 13.0 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  0.768 GPa
@Strain 9.60 %,
Temperature 0.000 °C		 111 ksi
@Strain 9.60 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  0.840 GPa
@Strain 0.500 %,
Temperature 100 °C		 122 ksi
@Strain 0.500 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.872 GPa
@Strain 9.20 %,
Temperature -20.0 °C		 126 ksi
@Strain 9.20 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  0.975 GPa
@Strain 1.20 %,
Temperature 80.0 °C		 141 ksi
@Strain 1.20 %,
Temperature 176 °F		 ISO 11403-1 -2
  1.75 GPa
@Strain 2.40 %,
Temperature 23.0 °C		 254 ksi
@Strain 2.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  1.775 GPa
@Strain 2.00 %,
Temperature 40.0 °C		 257.4 ksi
@Strain 2.00 %,
Temperature 104 °F		 ISO 11403-1 -2
  2.17 GPa
@Strain 2.40 %,
Temperature 0.000 °C		 314 ksi
@Strain 2.40 %,
Temperature 32.0 °F		 ISO 11403-1 -2
  2.5087 GPa
@Strain 2.30 %,
Temperature -20.0 °C		 363.86 ksi
@Strain 2.30 %,
Temperature -4.00 °F		 ISO 11403-1 -2
  2.96 GPa
@Strain 2.10 %,
Temperature -40.0 °C		 429 ksi
@Strain 2.10 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  14.0 kJ/m² 6.66 ft-lb/in² ISO 180/1A
  12.0 kJ/m²
@Temperature -40.0 °C		 5.71 ft-lb/in²
@Temperature -40.0 °F		 ISO 180/1A
Charpy Impact Unnotched  NB NB ISO 179/1eU
  35.0 J/cm²
@Temperature -30.0 °C		 167 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  1.40 J/cm² 6.66 ft-lb/in² ISO 179/1eA
  1.10 J/cm²
@Temperature -30.0 °C		 5.23 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2700 MPa
@Time 3600 sec		 392000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1500 MPa
@Time 3.60e+6 sec		 218000 psi
@Time 1000 hour		 ISO 899-1
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
Melting Point  178 °C 352 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  160 °C 320 °F ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  93.0 °C 199 °F ISO 75-1/-2
Vicat Softening Point  160 °C 320 °F 50°C/h 50N; ISO 306
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
 
Descriptive Properties
Additives Lubricants  
  Release agent  
Delivery form Pellets  
Part Marking Code >POM< ISO 11469
Processing Injection Moulding  
  Other Extrusion  
  Profile Extrusion  
  Sheet Extrusion  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification POM ISO 1043
UL recognition UL  
  UL
图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38518.html

免责声明: 本文 杜邦高性能聚合物聚甲醛POM fg100p NC010 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4