类别：聚合物；热塑性；聚甲醛（POM）
材料说明：1000是我们aartel优质钢化冲击改性缩醛共聚物。aartel 1000具有高冲击性能结合扩展的力学性能和高温抗腐蚀性化学品，燃料和碳氢化合物的配方。
物性表：
图：物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO 294-4 |
| Melt Flow | 2.97 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.97 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | (50mm/min); ISO 527-2/1A |
| Elongation at Yield | 14 % | 14 % | (50mm/min); ISO 527-2/1A |
| Tensile Modulus | 1.75 GPa | 254 ksi | (1mm/min); ISO 527-2/1A |
| Flexural Modulus | 1.62 GPa | 235 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1e |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1e | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 164 °C | 327 °F | (10°C/min); ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75-1/-2 |