类别：聚合物；热塑性；聚甲醛（POM）
材料说明：®共聚级M140是高流动量，通用注塑级。它是专为需要使用一些增强流动特性的标准®M90材料的应用特点。
通用，改进流程
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Density of Compound | 1.20 g/cc | 0.0434 lb/in³ | melt; Internal | ||
| Water Absorption | 0.75 % | 0.75 % | ISO 62 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| 0.022 cm/cm | 0.022 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ISO 294-4 | ||
| 0.018 cm/cm | 0.018 in/in | ASTM D955 | |||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.7 MPa | 8800 psi | ASTM D638 | ||
| 65.0 MPa | 9430 psi | 50mm/min; ISO 527-2/1A | |||
| 34.5 MPa @Temperature 71.1 °C |
5000 psi @Temperature 160 °F |
ASTM D638 | |||
| 94.5 MPa @Temperature -40.0 °C |
13700 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.74 GPa | 397 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.64 GPa | 383 ksi | ISO 178 | ||
| 0.689 GPa @Temperature 104 °C |
100 ksi @Temperature 220 °F |
ASTM D790 | |||
| 1.24 GPa @Temperature 71.1 °C |
180 ksi @Temperature 160 °F |
ASTM D790 | |||
| 2.59 GPa @Temperature 22.8 °C |
375 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 | ||
| 0.481 J/cm @Temperature -40.0 °C |
0.900 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |||
| Izod Impact, Notched (ISO) | 5.70 kJ/m² | 2.71 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1 hour | 2350 MPa | 341000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| Specific Heat Capacity | 2.21 J/g-°C | 0.528 BTU/lb-°F | Internal | ||
| Thermal Conductivity | 0.155 W/m-K | 1.08 BTU-in/hr-ft²-°F | Internal | ||
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ISO 75-1, -2 | ||
| 110 °C | 230 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | generally preferred range, may vary with thickness | ||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 180 - 200 °C | 356 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow-medium | ||||
| Pellets | Yes | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||
| Processing conditions | ISO 9988-2 | ||||
| Profile extrusion | No | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com