类别：聚合物；热塑性；聚甲醛（POM）；乙缩醛共聚物，矿物填充
材料说明：特点：®共聚级MC90是矿物增强级提供低翘曲刚度，提高尺寸稳定性，改进，改进的实际影响和良好的成型性能的基体树脂性能的保留。
矿产耦合减少翘曲，通用级
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 | ||
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.75 % | 0.75 % | ISO 62 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | ASTM D955 | ||
| 0.019 cm/cm | 0.019 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | ASTM D955 | ||
| 0.016 cm/cm | 0.016 in/in | ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 | ||
| 57.0 MPa | 8270 psi | 50mm/min; ISO 527-2/1A | |||
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.85 GPa | 413 ksi | ISO 178 | ||
 |
2.96 GPa @Temperature 22.8 °C |
430 ksi @Temperature 73.0 °F |
ASTM D790 | ||
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.30 kJ/m² | 3.00 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.680 J/cm² | 3.24 ft-lb/in² | ISO 179/1eA | ||
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 165 °C | 329 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 165 °C | 329 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 | ||
| 97.0 °C | 207 °F | ISO 75-1, -2 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Die Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 180 - 200 °C | 356 - 392 °F | |||
| Mold Temperature | 82.2 - 93.3 °C | 180 - 200 °F | generally preferred range, may vary with thickness | ||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Dry Time | 3.00 hour | 3.00 hour | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 0.500 MPa | 72.5 psi | |||
| Hot-Working Temperature | 190 - 200 °C | 374 - 392 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow | ||||
| Pellets | Yes | ||||
| Processing conditions | ISO 9988-2 | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com