类别：聚合物；热塑性；聚甲醛（POM）
材料说明：化学缩写根据ISO 1043-1：POM
注塑成型和挤出成型
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Density of Compound | 1.20 g/cc | 0.0434 lb/in³ | melt; Internal | ||
| Water Absorption | 0.65 % | 0.65 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 32 % | 32 % | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 9.0 % | 9.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 22.0 J/cm² | 105 ft-lb/in² | partial; ISO 179/1eU | ||
| 20.0 J/cm² @Temperature -30.0 °C |
95.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 2300 MPa | 334000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 1100 MPa | 160000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | ||
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0015 @Frequency 100 Hz |
0.0015 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 | ||
| Specific Heat Capacity | 2.21 J/g-°C | 0.528 BTU/lb-°F | Internal | ||
| Thermal Conductivity | 0.155 W/m-K | 1.08 BTU-in/hr-ft²-°F | Internal | ||
| Melting Point | 165 °C | 329 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL94 | ||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL94 | |||
| Flame Spread | <= 75 mm/min | <= 3.0 in/min | ISO 3795 and FMVSS 302 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| 165 °C | 329 °F | Ejection temperature; Internal | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 190 - 200 °C | 374 - 392 °F | |||
| Zone 4 | 190 - 210 °C | 374 - 410 °F | |||
| Die Temperature | 190 - 210 °C | 374 - 410 °F | |||
| Melt Temperature | 180 - 190 °C | 356 - 374 °F | |||
| 190 - 210 °C | 374 - 410 °F | ||||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | ||||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | |||
| Moisture Content | 0.15 % | 0.15 % | Necessary low maximum residual | ||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 4.00 MPa | 580 psi | |||
| Screw Speed | 70 rpm @Diameter 55.0 mm |
70 rpm @Diameter 2.17 in |
|||
| 100 rpm @Diameter 40.0 mm |
100 rpm @Diameter 1.57 in |
||||
| 150 rpm @Diameter 25.0 mm |
150 rpm @Diameter 0.984 in |
||||
| Hot-Working Temperature | 190 - 210 °C | 374 - 410 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | slow-medium | ||||
| Longer pre-drying times/storage | Can be stored in standard conditions until processed. | ||||
| Pre-drying | Drying is not normally required with proper storage | ||||
| Processing conditions | 9988 | ||||
| Processing Notes | screws (minimum 25 D) will fit. | ||||
| screws (minimum 25 D) will fit. | |||||
| screws (minimum 25 D) will fit. | |||||
| screws (minimum 25 D) will fit. | |||||
| Profile extrusion | Yes | ||||
| Sheet extrusion | Yes | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com