POM C 9021 GV3 / 20 20%玻璃纤维增强_产品资讯

塞拉尼斯Hostaform®C 9021 GV3 / 20 POM ，20%玻璃纤维增强

类别：聚合物；热塑性；聚甲醛（POM）；共聚甲醛，20%玻璃纤维增强

材料说明：化学缩写根据ISO 1043-1：POM

注塑级，增强了约20%个玻璃球

物性表：

Physical Properties	Metric	English	Comments

Density	1.53 g/cc	0.0553 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	ISO 62
Melt Flow	8.5 g/10 min @Load 2.16 kg, Temperature 190 °C	8.5 g/10 min @Load 4.76 lb, Temperature 374 °F	(MVR) cm³/10min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa	6670 psi	50mm/min; ISO 527-2/1A
Elongation at Break	15 %	15 %	50mm/min; ISO 527-2/1A
Elongation at Yield	6.5 %	6.5 %	50mm/min; ISO 527-2/1A
Tensile Modulus	3.40 GPa	493 ksi	1mm/min; ISO 527-2/1A
Flexural Modulus	3.20 GPa	464 ksi	ISO 178
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²	ISO 179/1eU
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179/1eA
	0.350 J/cm² @Temperature -30.0 °C	1.67 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	3000 MPa	435000 psi	ISO 899-1
Tensile Creep Modulus, 1000 hours	1700 MPa	247000 psi	ISO 899-1

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	IEC 60093
Dielectric Constant	4.2 @Frequency 1.00e+6 Hz	4.2 @Frequency 1.00e+6 Hz	IEC 60250
	4.5 @Frequency 100 Hz	4.5 @Frequency 100 Hz	IEC 60250
Dielectric Strength	35.0 kV/mm	889 kV/in	IEC 60243-1
Dissipation Factor	0.0070 @Frequency 1.00e+6 Hz	0.0070 @Frequency 1.00e+6 Hz	IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-2
Melting Point	166 °C	331 °F	10°C/min; ISO 11357-1,-2,-3
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	ISO 75-1, -2
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	UL94
	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in	UL94
Flame Spread	<= 100 mm/min	<= 3.94 in/min	ISO 3795 and FMVSS 302

Processing Properties	Metric	English	Comments
Processing Temperature	20.0 - 30.0 °C	68.0 - 86.0 °F
	80.0 - 120 °C	176 - 248 °F	Cavity temperature
Feed Temperature	60.0 - 80.0 °C	140 - 176 °F
Zone 1	170 - 180 °C	338 - 356 °F
Zone 2	180 - 190 °C	356 - 374 °F
Zone 3	190 - 200 °C	374 - 392 °F
Zone 4	190 - 210 °C	374 - 410 °F
Die Temperature	190 - 210 °C	374 - 410 °F
Melt Temperature	190 - 230 °C	374 - 446 °F
Mold Temperature	80.0 - 120 °C	176 - 248 °F
Drying Temperature	100 - 120 °C	212 - 248 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour
Moisture Content	0.15 %	0.15 %	Necessary low maximum residual
Injection Pressure	60.0 - 120 MPa	8700 - 17400 psi
Hold Pressure	60.0 - 120 MPa	8700 - 17400 psi
Back Pressure	2.00 MPa	290 psi
Screw Speed	70 rpm @Diameter 55.0 mm	70 rpm @Diameter 2.17 in
	100 rpm @Diameter 40.0 mm	100 rpm @Diameter 1.57 in
	150 rpm @Diameter 25.0 mm	150 rpm @Diameter 0.984 in
Hot-Working Temperature	190 - 210 °C	374 - 410 °F

Descriptive Properties
Injection molding	Yes
Injection speed	slow
Longer pre-drying times/storage	The product can then be stored in standard conditions until processed.
Pre-drying	Drying is not normally required with proper storage
Processing conditions	ISO 9988

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！

我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！

如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！

欢迎新老客户来电咨询;

联系人：李先生

联系电话；13636696005

联系QQ；1020580970

联系邮箱；1020580970@qq.com