类别：聚合物；热塑性；聚甲醛（POM）
材料说明：Hostaform®lw15ewx是一家专业的低磨损等级的乙缩醛共聚物用于改进性能包括配对时，对其他热塑性树脂（PBT，PA，PC，PMMA）或钢。由于特殊的蜡混合材料具有良好的焊接线
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
(MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 32 % | 32 % | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 19 % | 19 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.65 GPa | 384 ksi | 1mm/min; ISO 527-2/1A | ||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA | ||
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 173 °C | 343 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| De |
|||||
| Injection molding | Yes | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com