类别：聚合物；热塑性；聚甲醛（POM）；乙缩醛共聚物，无筋
材料说明：Celcon共聚甲醛等级fg40u01是专门开发产品的非编织纤维生产使用熔喷加工技术。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | at 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.65 % | 0.65 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ISO 294-4 | ||
| Melt Flow | 40 g/10 min | 40 g/10 min | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 67.0 MPa | 9720 psi | 50 mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.83 GPa | 410 ksi | 1 mm/min; ISO 527-2/1A | ||
| Flexural Modulus | 2.82 GPa | 409 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.60 kJ/m² | 2.19 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.420 J/cm² | 2.00 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 165 °C | 329 °F | ISO 11357-1,2,3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 182 °C | 360 °F | |||
| Zone 2 | 193 °C | 380 °F | |||
| Zone 3 | 193 °C | 380 °F | |||
| Zone 4 | 193 °C | 380 °F | |||
| Die Temperature | 193 °C | 380 °F | |||
| De |
|||||
| Air Pressure | 8 psi | Processing Condition | |||
| Air Temperature | 400°F | Processing Condition | |||
| Die to Collector Distance | 7 in | Processing Condition | |||
| Melt Pressure | 500 psi | Processing Condition |
|||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com