帕克 PEI-140,高电磁屏蔽导电塑料的温度

PEI-140 帕克Chomerics总理™pei-140高电磁屏蔽导电塑料的温度 分类:聚合物 材料说明:pei-140提供了通过消除二次手术,如装配,成本下降65%的加工,油漆/电镀以及伴随这些过程的物流。 联系人: 夏先生 手 机: 13501802636 QQ :205730283 邮 箱 :205730283@qq.com
 PEI-140 的物性表:
 
Physical Properties Metric English Comments
Specific Gravity  1.61 g/cc 1.61 g/cc ASTM D792
Linear Mold Shrinkage  0.0065 cm/cm
@Thickness 3.17 mm
0.0065 in/in
@Thickness 0.125 in
ASTM D995
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  103 MPa 15000 psi ASTM D638
Elongation at Break  4.3 % 4.3 % ASTM D638
Flexural Strength  138 MPa 20000 psi ASTM D790
Flexural Modulus  8.20 GPa 1190 ksi ASTM D790
Izod Impact, Notched  0.600 J/cm 1.12 ft-lb/in ASTM D412
Izod Impact, Unnotched  2.10 J/cm 3.93 ft-lb/in ASTM D412
Impact  0.84
@Temperature 23.0 °C
0.84
@Temperature 73.4 °F
[ft-lb/in], Charpy; ASTM D6110-05a
 
Electrical Properties Metric English Comments
Surface Resistance  0.38 ohm 0.38 ohm  
Surface Resistivity per Square  0.45 ohm 0.45 ohm MIL-DTL-83528C
Shielding Effectiveness    60 dB
@Frequency 3.00e+7 Hz
60 dB
@Frequency 3.00e+7 Hz
ASTM D4935
  64 dB
@Frequency 1.00e+8 Hz
64 dB
@Frequency 1.00e+8 Hz
ASTM D4935
  85 dB
@Frequency 1.00e+9 Hz
85 dB
@Frequency 1.00e+9 Hz
ASTM D4935
   72 dB
@Thickness 1.80 mm,
Frequency 3.00e+7 - 1.00e+9 Hz
72 dB
@Thickness 0.0709 in,
Frequency 3.00e+7 - 1.00e+9 Hz
ASTM D4935
  80 dB
@Thickness 1.80 mm,
Frequency 8.00e+8 - 1.80e+10 Hz
80 dB
@Thickness 0.0709 in,
Frequency 8.00e+8 - 1.80e+10 Hz
IEEE 299
 
Thermal Properties Metric English Comments
Thermal Conductivity  0.710 W/m-K 4.93 BTU-in/hr-ft²-°F ASTM D5470
Deflection Temperature at 1.8 MPa (264 psi)  363 °C 685 °F ASTM D648
Flammability, UL94  V-0
@Thickness 1.80 mm
V-0
@Thickness 0.0709 in
 
NBS Smoke Density  <= 110
@Thickness 3.00 mm,
Time 240 sec
<= 110
@Thickness 0.118 in,
Time 0.0667 hour
[Ds]; BSS 7238/7239
Oxygen Index  41 % 41 % Limited; ASTM D2863
 
Processing Properties Metric English Comments
Rear Barrel Temperature  360 - 385 °C 680 - 725 °F  
Front Barrel Temperature  370 - 395 °C 698 - 743 °F  
Nozzle Temperature  370 - 395 °C 698 - 743 °F  
Melt Temperature  370 - 395 °C 698 - 743 °F  
Mold Temperature  90.0 - 115 °C 194 - 239 °F  
Dry Time    5 - 7 hour
@Temperature 150 - 160 °C
5 - 7 hour
@Temperature 302 - 320 °F
Typical
  24.0 hour
@Temperature 150 - 160 °C
24.0 hour
@Temperature 302 - 320 °F
Maximum
Moisture Content  0.020 % 0.020 % Suggested Maximum
Back Pressure  0.517 - 0.862 MPa 75.0 - 125 psi  
Clamp Pressure  55.0 - 80.0 MPa 7980 - 11600 psi [Mpa/cm2]
Cushion  1.02 - 1.27 cm 0.400 - 0.500 in  
Screw Speed  95 - 130 rpm
@Diameter 25.4 mm
95 - 130 rpm
@Diameter 1.00 in
760 - 1000 cm/min
 

上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636  021 51131842
QQ    :205730283  
邮 箱 :205730283@qq.com 

PEI-140 图:

 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-38810.html

免责声明: 本文 帕克 PEI-140,高电磁屏蔽导电塑料的温度 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4