| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.65 % | 0.65 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0017 cm/cm | 0.0017 in/in | ISO 294-4 | ||
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 190 °C |
18 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527-2/1A | ||
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-2/1A | ||
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 | ||
| Shear Modulus | 100 GPa @Temperature 150 °C |
14500 ksi @Temperature 302 °F |
|||
| 200 GPa @Temperature 100 °C |
29000 ksi @Temperature 212 °F |
||||
| 300 GPa @Temperature 50.0 °C |
43500 ksi @Temperature 122 °F |
||||
| 800 GPa @Temperature 0.000 °C |
116000 ksi @Temperature 32.0 °F |
||||
| 1200 GPa @Temperature -50.0 °C |
174000 ksi @Temperature -58.0 °F |
||||
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature -30.0 °C |
52.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
Partial break; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | ||
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 800 MPa | 116000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 4.4 @Frequency 100 Hz |
4.4 @Frequency 100 Hz |
IEC 60250 | ||
| 4.4 @Frequency 1.00e+6 Hz |
4.4 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 1.30 µm/m-°C | 0.722 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Nozzle Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Zone 1 | 170 - 180 °C | 338 - 356 °F | |||
| Zone 2 | 180 - 190 °C | 356 - 374 °F | |||
| Zone 3 | 190 - 200 °C | 374 - 392 °F | |||
| Zone 4 | 190 - 200 °C | 374 - 392 °F | |||
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Mold Temperature | 60.0 - 70.0 °C | 140 - 158 °F | |||
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Hold Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Back Pressure | 0.000 - 2.00 MPa | 0.000 - 290 psi | |||
| Screw Speed | 70 rpm @Diameter 55.0 mm |
70 rpm @Diameter 2.17 in |
|||
| 100 rpm @Diameter 40.0 mm |
100 rpm @Diameter 1.57 in |
||||
| 150 rpm @Diameter 25.0 mm |
150 rpm @Diameter 0.984 in |
||||
| De |
|||||
| Hopper | 20-30°C | ||||
| Manifold | 190-200°C | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询;
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com