| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 | ||
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 | ||
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.25 % | 1.25 % | ASTM D570 | ||
| Water Absorption at Saturation | 1.25 % | 1.25 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method | ||
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow | 12 g/10 min @Load 6.60 kg, Temperature 337 °C |
12 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 | ||
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 360 °C |
17 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 | ||
| 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 | ||
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |||
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 | ||
| 60 % | 60 % | 5 mm/min; ISO 527 | |||
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 | ||
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 | ||
| 3.59 GPa | 521 ksi | 5 mm/min; ASTM D638 | |||
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 | ||
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 | ||
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| 13.35 J/cm @Thickness 3.20 mm |
25.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |||
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U | ||
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| Dart Drop, Total Energy | 38.0 J @Temperature 23.0 °C |
28.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | ||
| 55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | ||
| 55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |||
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C177 | ||
| 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | |||
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |||
| 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |||
| 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |||
| 201 °C @Thickness 6.40 mm |
394 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |||
| Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ISO 306 | ||
| 212 °C | 414 °F | Rate B/120; ISO 306 | |||
| 215 °C | 419 °F | Rate A/50; ISO 306 | |||
| 219 °C | 426 °F | Rate B/50; ASTM D1525 | |||
| Glass Transition Temp, Tg | 217 °C | 423 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified | ||
| De |
|||||
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
|||
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
PEI 1000EF 图：