LG Chemical LUCEL N145LD 注塑级_产品资讯

物性表：

Physical Properties	Metric	English	Comments

Specific Gravity	1.41 g/cc	1.41 g/cc	ASTM D792
Maximum Moisture Content	0.10	0.10	Injection Molding
Linear Mold Shrinkage, Flow	0.018 - 0.021 cm/cm @Thickness 3.20 mm	0.018 - 0.021 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	45 g/10 min @Load 2.16 kg, Temperature 190 °C	45 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	82	82	ASTM D785
Tensile Strength, Yield	62.3 MPa @Thickness 3.20 mm	9030 psi @Thickness 0.126 in	10mm/min; ASTM D638
Elongation at Break	50 % @Thickness 3.20 mm	50 % @Thickness 0.126 in	10mm/min; ASTM D638
Flexural Yield Strength	93.2 MPa @Thickness 6.40 mm	13500 psi @Thickness 0.252 in	2.8mm/min; ASTM D790
Flexural Modulus	2.65 GPa @Thickness 6.40 mm	384 ksi @Thickness 0.252 in	2.8mm/min; ASTM D790
Izod Impact, Notched	0.539 J/cm @Thickness 6.40 mm, Temperature 23.0 °C	1.01 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	3.8 @Frequency 1.00e+6 Hz	3.8 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	24.0 kV/mm @Thickness 1.00 mm	610 kV/in @Thickness 0.0394 in	ASTM D149
Hot Wire Ignition, HWI	0.00 - 7.0 sec @Thickness >=0.710 mm	0.00 - 7.0 sec @Thickness >=0.0280 in
	0.00 - 7.0 sec @Thickness >=1.50 mm	0.00 - 7.0 sec @Thickness >=0.0591 in
	7.0 - 15 sec @Thickness >=3.00 mm	7.0 - 15 sec @Thickness >=0.118 in
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.710 mm	>= 120 arcs @Thickness 0.0280 in
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	160 °C @Thickness 6.40 mm	320 °F @Thickness 0.252 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	110 °C @Thickness 6.40 mm	230 °F @Thickness 0.252 in	Unannealed; ASTM D648
UL RTI, Electrical	110 °C @Thickness >=0.710 mm	230 °F @Thickness >=0.0280 in
	110 °C @Thickness >=1.50 mm	230 °F @Thickness >=0.0591 in
	110 °C @Thickness >=3.00 mm	230 °F @Thickness >=0.118 in
UL RTI, Mechanical with Impact	95.0 °C @Thickness >=0.710 mm	203 °F @Thickness >=0.0280 in
	95.0 °C @Thickness >=1.50 mm	203 °F @Thickness >=0.0591 in
	95.0 °C @Thickness >=3.00 mm	203 °F @Thickness >=0.118 in
UL RTI, Mechanical without Impact	90.0 °C @Thickness >=0.710 mm	194 °F @Thickness >=0.0280 in
	95.0 °C @Thickness >=1.50 mm	203 °F @Thickness >=0.0591 in
	100 °C @Thickness >=3.00 mm	212 °F @Thickness >=0.118 in
Flammability, UL94	HB @Thickness >=0.710 mm	HB @Thickness >=0.0280 in
	HB @Thickness >=1.50 mm	HB @Thickness >=0.0591 in
	HB @Thickness >=3.00 mm	HB @Thickness >=0.118 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	160 - 180 °C	320 - 356 °F	Injection Molding
Middle Barrel Temperature	180 - 200 °C	356 - 392 °F	Injection Molding
Front Barrel Temperature	190 - 200 °C	374 - 392 °F	Injection Molding
Nozzle Temperature	190 - 200 °C	374 - 392 °F	Injection Molding
Melt Temperature	190 - 200 °C	374 - 392 °F	Injection Molding
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F	Injection Molding
Drying Temperature	90.0 - 110 °C	194 - 230 °F	Injection Molding
Dry Time	3.00 - 6.00 hour	3.00 - 6.00 hour	Injection Molding
Back Pressure	4.02 - 8.04 MPa	583 - 1170 psi	Injection Molding
Screw Speed	50 - 100 rpm	50 - 100 rpm	Injection Molding

图：

上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！

我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！

主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！

欢迎新老客户来电或QQ咨询：

联系人：李先生

联系电话；13636696005

联系QQ；1020580970

联系邮箱；1020580970@qq.com