| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 253 °C | 487 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
下图仅供参考（非实物图）：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。