| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | |
| Water Absorption | 2.3 % | 2.3 % | |
| Moisture Absorption at Equilibrium | 1.05 % | 1.05 % | Humidity Absorption |
| Melt Flow | 9.5 g/10 min @Load 2.16 kg, Temperature 275 °C |
9.5 g/10 min @Load 4.76 lb, Temperature 527 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min |
| Elongation at Break | 3.1 % | 3.1 % | 5 mm/min |
| Tensile Modulus | 5.50 GPa | 798 ksi | 1 mm/min |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
||
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
下图仅供参考（非实物图）：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。