| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 8.5 % | 8.5 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 3.5 cP | 3.5 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 205 cm³/g | 205 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM Data; MD | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C |
40 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Tensile Creep Modulus, 1 hour | 1100 MPa | 160000 psi | ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz |
0.20 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 255 °C | 491 °F | 10 K/min | ||
| 260 °C | 500 °F | ASTM Test | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Film Extrusion | ||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。
下图仅供参考（非实物图）：
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。