| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
| 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.290 % | 0.290 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D955 |
| 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO 527 |
| 56.0 MPa | 8120 psi | ASTM D638 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| 56.0 MPa | 8120 psi | ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| 4.0 % | 4.0 % | ISO 527 | |
| Elongation at Yield | 2.3 % | 2.3 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Tensile Modulus | 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 |
| 6.13 GPa | 889 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 92.0 MPa | 13300 psi | ASTM D790 |
| 92.0 MPa | 13300 psi | ISO 178 | |
| Flexural Modulus | 5.30 GPa | 769 ksi | ASTM D790 |
| 6.30 GPa | 914 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 1850 x 10-8 mm³/N-M | 920 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com