| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.027 - 0.031 cm/cm @Time 86400 sec |
0.027 - 0.031 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.021 - 0.024 cm/cm @Time 86400 sec |
0.021 - 0.024 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 2.07 GPa | 300 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 48.0 MPa | 6960 psi | ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.10 | 0.10 | ASTM D 3702 Modified |
| K (wear) Factor | 2.01 x 10-8 mm³/N-M | 1.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com