POM俗名聚甲醛，是一种用途非常广泛的材料，外观呈半透明或者不透明的颗粒状，与象牙有点相似。
聚甲醛在较大的温度范围内具有较高的弹性模数、硬度、刚性和机械性能，可在104℃以下长期使用，脆化温度-40℃，吸水性极小。有“塑料中的金属”之称。
可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等
物性表：
图：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm @Time 86400 sec |
0.023 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0233 cm/cm @Time 86400 sec |
0.0233 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0224 cm/cm @Time 86400 sec |
0.0224 in/in @Time 24.0 hour |
ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ISO 527 |
| 37.0 MPa | 5370 psi | ASTM D 638 | |
| Elongation at Break | 12 % | 12 % | ISO 527 |
| 17 % | 17 % | ASTM D 638 | |
| Tensile Modulus | 3.70 GPa | 537 ksi | 1 mm/min; ISO 527 |
| 3.72 GPa | 540 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D 790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 2.89 GPa | 419 ksi | ASTM D 790 |
| 3.30 GPa | 479 ksi | ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.93 J/cm @Temperature 23.0 °C |
5.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com