| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO R 1183 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | DIN 53473 | ||
| Water Absorption at Saturation | 0.60 % @Temperature 20.0 °C |
0.60 % @Temperature 68.0 °F |
ISO R 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 135 MPa | 19600 psi | Hc 30; ISO 2039; partially | ||
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | ISO-DIS 527 | ||
| Creep Strength | 13.0 MPa | 1890 psi | 1% elongation, 1000 h; DIN 53444 | ||
| 22.0 MPa | 3190 psi | 2% elongation, 1000 h; DIN 53444 | |||
| Tensile Modulus | 3.50 GPa | 508 ksi | DIN 53457 | ||
| Flexural Strength | 117 MPa | 17000 psi | DIN 54352 | ||
| Flexural Modulus | 3.00 GPa | 435 ksi | DIN 53457 | ||
| Compressive Strength | 50.0 MPa | 7250 psi | 5% pressing; EN ISO 604 | ||
| 83.0 MPa | 12000 psi | 10% pressing; EN ISO 604 | |||
| 103 MPa | 14900 psi | 20% pressing; EN ISO 604 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | DIN 53453 | ||
| Izod Impact Resistance | >= 9.00 J/cm² | >= 42.8 ft-lb/in² | swinging hammer 0,1 DIN 51222; DIN 53453 | ||
| Coefficient of Friction | 0.020 - 0.080 | 0.020 - 0.080 | With lubrication | ||
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C | ||
| Tear Strength Test | 0.60 | 0.60 | ISO-DIS 527 | ||
| K Factor (Wear Factor) | 9.00e-10 | 9.00e-10 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 | ||
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 | ||
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | DIN 53481 | ||
| Dielectric Loss Index | 0.0035 | 0.0035 | DIN 53483 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 100 µm/m-°C @Temperature 20.0 - 100 °C |
55.6 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 | ||
| Specific Heat Capacity | 1.46 J/g-°C | 0.349 BTU/lb-°F | |||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 167 °C | 333 °F | ISO R 1218 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous | ||
| 140 °C | 284 °F | Intermittent | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | V-notch; ISO R 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | V-notch; ISO R 75 | ||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous | ||
| De |
|||||
| Creepage/leakage Resistance | KA3b | DIN 53480 |
|||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com