| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.7 - 5.3 % | 4.7 - 5.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.0 - 1.4 % | 1.0 - 1.4 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | restricted | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 105 MPa | 15200 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 6.50 GPa | 943 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | ||
| 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00 Hz |
3.8 @Frequency 1.00 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Test solution A; IEC 60112 | ||
| Hot Wire Ignition, HWI | 0.00 sec @Thickness >=0.750 mm |
0.00 sec @Thickness >=0.0295 in |
ASTM D3874-88 | ||
| High Amp Arc Ignition, HAI | 0.00 arcs @Thickness >=0.750 mm |
0.00 arcs @Thickness >=0.0295 in |
UL 746C | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 - 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 16.7 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
33.3 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 180 °C | 356 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| UL RTI, Electrical | 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0591 in |
UL 746B | ||
| Flammability, UL94 | V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
|||
| 5VB @Thickness >=2.30 mm |
5VB @Thickness >=0.0906 in |
||||
| Oxygen Index | 28 % | 28 % | ISO 4589-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 290 °C | 554 °F | Feed Zone | ||
| Zone 2 | 290 °C | 554 °F | Compression | ||
| Zone 3 | 290 °C | 554 °F | Metering-zone | ||
| Zone 4 | 290 °C | 554 °F | Nozzle | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| 290 °C | 554 °F | Optimal | |||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection-molding | ||
| 80.0 °C | 176 °F | Optimal | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| De |
|||||
| Color | BK 23187 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||
PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。
下图仅供参考（非实物图）：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com