| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 4.1 % | 4.1 % | ISO 527 | ||
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527 | ||
| Flexural Modulus | 4.40 GPa | 638 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180 | ||
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 288 - 305 °C | 550 - 581 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Dry Time | 1 - 2 hour | 1 - 2 hour | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| De |
|||||
| Color | BK 20465 | ||||
| Commercial Status | North America | ||||
性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。
下图仅供参考（非实物图）：
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。