类别：聚合物；热塑性塑料；尼龙；尼龙66；尼龙66，30%玻璃纤维填充
材料说明：Ultramid 1503-2f BK nd3007是33%玻璃纤维增强，热稳定尼龙注塑/ 6级。它的目的是提供提高酶解反应电阻内部应用。
物性表：| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50% RH; ISO 178 | ||
| 5.7 % | 5.7 % | Saturation; ISO 178 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 10.8 GPa | 1570 ksi | ISO 527 | ||
Charpy Impact, Notched  |
0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | ||
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 288 - 305 °C | 550 - 581 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 1 - 2 hour | 1 - 2 hour | |||
| Moisture Content | 0.040 - 0.20 % | 0.040 - 0.20 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| De |
|||||
| Color | BK ND 3007 | ||||
| Commercial Status | North America | ||||
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com